Copper Alloy C32000-H02 vs C32000-O60
Copper Alloy · C32000 temper comparison
C32000-H02 and C32000-O60 are two conditions of the same copper alloy grade, C32000: H02 (half hard) versus O60 (soft annealed). The chemistry is identical, so every difference below comes from the condition. C32000-H02 is the stronger of the two: yield strength 270 MPa (39.2 ksi) against 95 MPa (13.8 ksi) for C32000-O60, about 184% more; tensile strength follows at 350 MPa (50.8 ksi) vs 275 MPa (39.9 ksi). In exchange, C32000-O60 is the more ductile: elongation 55% versus 25% for C32000-H02, and C32000-H02 is harder (100 HB vs 55 HB). C32000-O60 runs hotter in service (200°C vs 180°C continuous). On the shop floor, C32000-H02 machines more easily (80 vs 70 out of 100).
C32000-H02Choose it when strength drives the design, or when the part is machined in volume.
C32000-O60Choose it when the part is bent, formed or impact-loaded, or when the part sees heat.
C32000-H02 vs C32000-O60: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Rockwell B
Same in both: Elastic (Young's) Modulus 117 GPa17 Msi · Shear Modulus 44 GPa6.4 Msi · Bulk Modulus 120 GPa17.4 Msi · Poisson's Ratio 0.34
Physical
Density and transition temperatures.
Same in both: Density 8.75 g/cm³0.32 lb/in³ · Melting Point (Solidus) 980°C1,796 °F · Liquidus Temperature 1,010°C1,850 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 380 J/kg·K0.09 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 18.7 µm/m·K10.4 µin/in·°F · Latent Heat of Fusion 200 J/g86 BTU/lb · Min Service Temperature -200°C-328 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Same in both: Electrical Resistivity 4.8×10⁻⁸ Ω·m1.89 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.25 V · Corrosion Resistance 62 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Formability (cold)
Same in both: Weldability 20 / 100 · Castability 60 / 100 · Brazeability / Solderability 55 / 100 · Polishability 70 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 55 MJ/kg23,646 BTU/lb · Embodied Carbon (primary production) 3.6 kg CO₂/kg · Embodied Water 350 L/kg41.9 gal/lb · Typical Recycled Content 45%
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
C32000-H02 vs C32000-O60 — frequently asked
Is C32000-H02 stronger than C32000-O60?
Yes. C32000-H02 has a typical yield strength of 270 MPa (39.2 ksi) against 95 MPa (13.8 ksi) for C32000-O60 — about 184% more. Tensile strength is 350 MPa (50.8 ksi) vs 275 MPa (39.9 ksi).
Which condition does FabDigit quote by default, H02 or O60?
H02 is the default C32000 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, C32000-H02 or C32000-O60?
C32000-H02, by a small margin. Both rate very good for machinability — 80/100 against 70/100 for C32000-O60.