Copper Alloy C32000-H02 vs C32000-H80
Copper Alloy · C32000 temper comparison
C32000-H02 and C32000-H80 are two conditions of the same copper alloy grade, C32000: H02 (half hard) versus H80 (hard drawn). The chemistry is identical, so every difference below comes from the condition. C32000-H80 is the stronger of the two: yield strength 345 MPa (50 ksi) against 270 MPa (39.2 ksi) for C32000-H02, about 28% more; tensile strength follows at 415 MPa (60.2 ksi) vs 350 MPa (50.8 ksi). In exchange, C32000-H02 is the more ductile: elongation 25% versus 10% for C32000-H80, and C32000-H80 is harder (130 HB vs 100 HB). C32000-H02 runs hotter in service (180°C vs 150°C continuous).
C32000-H02Choose it when the part is bent, formed or impact-loaded, or when the part sees heat.
C32000-H80Choose it when strength drives the design.
C32000-H02 vs C32000-H80: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Rockwell B
Same in both: Elastic (Young's) Modulus 117 GPa17 Msi · Shear Modulus 44 GPa6.4 Msi · Bulk Modulus 120 GPa17.4 Msi · Poisson's Ratio 0.34
Physical
Density and transition temperatures.
Same in both: Density 8.75 g/cm³0.32 lb/in³ · Melting Point (Solidus) 980°C1,796 °F · Liquidus Temperature 1,010°C1,850 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 151 W/m·K87.2 BTU/hr·ft·°F · Specific Heat Capacity 380 J/kg·K0.09 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 18.7 µm/m·K10.4 µin/in·°F · Latent Heat of Fusion 200 J/g86 BTU/lb · Min Service Temperature -200°C-328 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.25 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Formability (cold)
Same in both: Weldability 20 / 100 · Castability 60 / 100 · Brazeability / Solderability 55 / 100 · Polishability 70 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 55 MJ/kg23,646 BTU/lb · Embodied Carbon (primary production) 3.6 kg CO₂/kg · Embodied Water 350 L/kg41.9 gal/lb · Typical Recycled Content 45%
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
C32000-H02 vs C32000-H80 — frequently asked
Is C32000-H80 stronger than C32000-H02?
Yes. C32000-H80 has a typical yield strength of 345 MPa (50 ksi) against 270 MPa (39.2 ksi) for C32000-H02 — about 28% more. Tensile strength is 415 MPa (60.2 ksi) vs 350 MPa (50.8 ksi).
Which condition does FabDigit quote by default, H02 or H80?
H02 is the default C32000 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
When should I choose C32000-H02 over C32000-H80?
Pick C32000-H02 when the part is bent, formed or impact-loaded, or when the part sees heat. Pick C32000-H80 when strength drives the design.
Ready to make it?
Upload a CAD file and FabDigit prices the part in C32000-H02 and C32000-H80 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.