Copper Alloy C28000 vs C49300
Copper Alloy · grade comparison
Copper Alloy C28000 and C49300 are both copper alloy grades. C49300 is the stronger of the two: yield strength 310 MPa (45 ksi) against 145 MPa (21 ksi) for C28000, about 114% more; tensile strength follows at 440 MPa (63.8 ksi) vs 372 MPa (54 ksi). In exchange, C28000 is the more ductile: elongation 45% versus 18% for C49300, and C49300 is harder (125 HB vs 75 HB). C28000 conducts heat better (123 W/m·K vs 110 W/m·K). On the shop floor, C49300 machines more easily (excellent vs good), C28000 welds better (fair vs poor), and C28000 sits in a lower cost tier (premium, $$$) than C49300 (high, $$$$).
C28000Choose it when the part is bent, formed or impact-loaded, or when it will be welded.
C49300Choose it when strength drives the design, or when the part is machined in volume.
C28000 vs C49300: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Rockwell B
Charpy V-Notch Impact (RT)
Hardness, Vickers
Same in both: Bulk Modulus 112 GPa16.2 Msi · Poisson's Ratio 0.34
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Min Service Temperature
Same in both: Max Service Temperature (continuous) 200°C392 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.28 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Brazeability / Solderability
Polishability
Same in both: Castability 55 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | C28000 | C49300 |
|---|---|---|
| CNC machining | Yes | — |
| Sheet metal | Yes | — |
| Default condition | O | — |
| Relative cost | $$$ Premium | $$$$ High |
| Min. machined wall | 0.8 mm | — |
| Best machined surface | Ra 1.6 µm | — |
| Chrome Plating | Yes | — |
| Electropolishing | Yes | — |
| Nickel Plating | Yes | — |
| Painting | Yes | — |
| Tin Plating | Yes | — |
They share 4 finishes: Copper Plating, Electroless Nickel (EN), Gold Plating, Silver Plating.
C28000 vs C49300 — frequently asked
Is C49300 stronger than C28000?
Yes. C49300 has a typical yield strength of 310 MPa (45 ksi) against 145 MPa (21 ksi) for C28000 — about 114% more. Tensile strength is 440 MPa (63.8 ksi) vs 372 MPa (54 ksi).
Which is cheaper, C28000 or C49300?
C28000 is the lower-cost material: it sits in the premium tier ($$$) while C49300 is high ($$$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, C28000 or C49300?
C49300. Its machinability rates excellent (88/100) against good (55/100) for C28000; for welding the order is C28000 first (fair, 50/100) then C49300 (poor, 30/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in C28000 and C49300 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.