Copper Alloy C28000 vs C35300
Copper Alloy · grade comparison
Copper Alloy C28000 and C35300 are both copper alloy grades. C35300 is the stronger of the two: yield strength 345 MPa (50 ksi) against 145 MPa (21 ksi) for C28000, about 138% more; tensile strength follows at 420 MPa (60.9 ksi) vs 372 MPa (54 ksi). In exchange, C28000 is the more ductile: elongation 45% versus 20% for C35300, and C35300 is harder (115 HB vs 75 HB). C28000 is stiffer (105 GPa vs 97 GPa) and C28000 runs hotter in service (200°C vs 150°C continuous). On the shop floor, C35300 machines more easily (very good vs good), C28000 welds better (fair vs poor), and C28000 sits in a lower cost tier (premium, $$$) than C35300 (high, $$$$).
C28000Choose it when the part is bent, formed or impact-loaded, or when the part sees heat.
C35300Choose it when strength drives the design, or when the part is machined in volume.
C28000 vs C35300: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Bulk Modulus 112 GPa16.2 Msi · Poisson's Ratio 0.34
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Min Service Temperature
Same in both: Latent Heat of Fusion 160 J/g68.8 BTU/lb
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.28 V · Corrosion Resistance 45 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Castability
Brazeability / Solderability
Same in both: Formability (cold) 55 / 100 · Polishability 75 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | C28000 | C35300 |
|---|---|---|
| Sheet metal | Yes | — |
| Default condition | O | H02 |
| Relative cost | $$$ Premium | $$$$ High |
| Min. machined wall | 0.8 mm | 0.8 mm |
| Best machined surface | Ra 1.6 µm | Ra 1.6 µm |
Both are offered for CNC machining. Both take the same 9 finishes: Chrome Plating, Copper Plating, Electroless Nickel (EN), Electropolishing, Gold Plating, Nickel Plating, Painting, Silver Plating, Tin Plating.
C28000 vs C35300 — frequently asked
Is C35300 stronger than C28000?
Yes. C35300 has a typical yield strength of 345 MPa (50 ksi) against 145 MPa (21 ksi) for C28000 — about 138% more. Tensile strength is 420 MPa (60.9 ksi) vs 372 MPa (54 ksi).
Which is cheaper, C28000 or C35300?
C28000 is the lower-cost material: it sits in the premium tier ($$$) while C35300 is high ($$$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, C28000 or C35300?
C35300. Its machinability rates very good (70/100) against good (55/100) for C28000; for welding the order is C28000 first (fair, 50/100) then C35300 (poor, 15/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in C28000 and C35300 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.