Copper Alloy C19100-M11 vs C19100-TF00
Copper Alloy · C19100 temper comparison
C19100-M11 and C19100-TF00 are two conditions of the same copper alloy grade, C19100: M11 (as forged and quenched) versus TF00 (solution heat treated and precipitation hardened). The chemistry is identical, so every difference below comes from the condition. C19100-TF00 is the stronger of the two: yield strength 400 MPa (58 ksi) against 140 MPa (20.3 ksi) for C19100-M11, about 186% more; tensile strength follows at 470 MPa (68.2 ksi) vs 310 MPa (45 ksi). In exchange, C19100-M11 is the more ductile: elongation 35% versus 15% for C19100-TF00, and C19100-TF00 is harder (140 HB vs 72 HB). C19100-TF00 runs hotter in service (300°C vs 200°C continuous) and C19100-TF00 conducts heat better (180 W/m·K vs 150 W/m·K).
C19100-M11Choose it when the part is bent, formed or impact-loaded.
C19100-TF00Choose it when strength drives the design, or when the part sees heat.
C19100-M11 vs C19100-TF00: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Hardness, Brinell
Hardness, Rockwell B
Same in both: Elastic (Young's) Modulus 121 GPa17.5 Msi · Shear Modulus 45 GPa6.5 Msi · Bulk Modulus 135 GPa19.6 Msi · Poisson's Ratio 0.34 · Reduction in Area 45% · Shear Strength 275 MPa39.9 ksi · Fatigue Strength (Endurance Limit) 165 MPa23.9 ksi · Charpy V-Notch Impact (RT) 30 J22.1 ft·lbf
Physical
Density and transition temperatures.
Same in both: Density 8.86 g/cm³0.32 lb/in³ · Melting Point (Solidus) 1,035°C1,895 °F · Liquidus Temperature 1,075°C1,967 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 377 J/kg·K0.09 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 17.6 µm/m·K9.8 µin/in·°F · Latent Heat of Fusion 205 J/g88.1 BTU/lb · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Same in both: Electrical Resistivity 3.83×10⁻⁸ Ω·m1.51 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.2 V · Corrosion Resistance 62 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability Rating (AISI 1212 = 100 %)
Formability (cold)
Same in both: Machinability 82 / 100 · Weldability 25 / 100 · Brazeability / Solderability 70 / 100 · Polishability 70 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 57 MJ/kg24,506 BTU/lb · Embodied Carbon (primary production) 3.8 kg CO₂/kg · Embodied Water 220 L/kg26.4 gal/lb · Typical Recycled Content 30%
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
C19100-M11 vs C19100-TF00 — frequently asked
Is C19100-TF00 stronger than C19100-M11?
Yes. C19100-TF00 has a typical yield strength of 400 MPa (58 ksi) against 140 MPa (20.3 ksi) for C19100-M11 — about 186% more. Tensile strength is 470 MPa (68.2 ksi) vs 310 MPa (45 ksi).
Which condition does FabDigit quote by default, M11 or TF00?
TF00 is the default C19100 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
When should I choose C19100-M11 over C19100-TF00?
Pick C19100-M11 when the part is bent, formed or impact-loaded. Pick C19100-TF00 when strength drives the design, or when the part sees heat.
Ready to make it?
Upload a CAD file and FabDigit prices the part in C19100-M11 and C19100-TF00 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.