Copper Alloy C19010-H01 vs C19010-TM04
Copper Alloy · C19010 temper comparison
C19010-H01 and C19010-TM04 are two conditions of the same copper alloy grade, C19010: H01 (quarter hard) versus TM04 (mill hardened, full hard). The chemistry is identical, so every difference below comes from the condition. C19010-TM04 is the stronger of the two: yield strength 480 MPa (69.6 ksi) against 340 MPa (49.3 ksi) for C19010-H01, about 41% more; tensile strength follows at 520 MPa (75.4 ksi) vs 400 MPa (58 ksi). In exchange, C19010-H01 is the more ductile: elongation 13% versus 8% for C19010-TM04, and C19010-TM04 is harder (155 HV vs 125 HV). C19010-TM04 runs hotter in service (200°C vs 150°C continuous).
C19010-H01Choose it when the part is bent, formed or impact-loaded.
C19010-TM04Choose it when strength drives the design, or when the part sees heat.
C19010-H01 vs C19010-TM04: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 131 GPa19 Msi · Shear Modulus 48 GPa7 Msi · Bulk Modulus 130 GPa18.9 Msi · Poisson's Ratio 0.34
Physical
Density and transition temperatures.
Same in both: Density 8.86 g/cm³0.32 lb/in³ · Melting Point (Solidus) 1,075°C1,967 °F · Liquidus Temperature 1,090°C1,994 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 385 J/kg·K0.09 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 17.6 µm/m·K9.8 µin/in·°F · Latent Heat of Fusion 205 J/g88.1 BTU/lb · Min Service Temperature -200°C-328 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Same in both: Electrical Resistivity 2.87×10⁻⁸ Ω·m1.13 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.2 V · Corrosion Resistance 55 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Formability (cold)
Same in both: Machinability Rating (AISI 1212 = 100 %) 60% · Weldability 45 / 100 · Brazeability / Solderability 90 / 100 · Polishability 70 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 57 MJ/kg24,506 BTU/lb · Embodied Carbon (primary production) 3.6 kg CO₂/kg · Embodied Water 250 L/kg30 gal/lb · Typical Recycled Content 30%
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
C19010-H01 vs C19010-TM04 — frequently asked
Is C19010-TM04 stronger than C19010-H01?
Yes. C19010-TM04 has a typical yield strength of 480 MPa (69.6 ksi) against 340 MPa (49.3 ksi) for C19010-H01 — about 41% more. Tensile strength is 520 MPa (75.4 ksi) vs 400 MPa (58 ksi).
Which condition does FabDigit quote by default, H01 or TM04?
TM04 is the default C19010 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, C19010-H01 or C19010-TM04?
C19010-TM04, by a small margin. Both rate fair for machinability — 40/100 against 35/100 for C19010-H01.
Ready to make it?
Upload a CAD file and FabDigit prices the part in C19010-H01 and C19010-TM04 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.