Copper Alloy C18600-TB00 vs C18600-TM06
Copper Alloy · C18600 temper comparison
C18600-TB00 and C18600-TM06 are two conditions of the same copper alloy grade, C18600: TB00 (solution heat treated) versus TM06 (mill hardened, extra hard). The chemistry is identical, so every difference below comes from the condition. C18600-TM06 is the stronger of the two: yield strength 560 MPa (81.2 ksi) against 95 MPa (13.8 ksi) for C18600-TB00, about 5.9 times as much; tensile strength follows at 590 MPa (85.6 ksi) vs 250 MPa (36.3 ksi). In exchange, C18600-TB00 is the more ductile: elongation 40% versus 6% for C18600-TM06, and C18600-TM06 is harder (175 HB vs 60 HB). C18600-TM06 runs hotter in service (350°C vs 150°C continuous) and C18600-TM06 conducts heat better (293 W/m·K vs 170 W/m·K).
C18600-TB00Choose it when the part is bent, formed or impact-loaded.
C18600-TM06Choose it when strength drives the design, or when the part sees heat.
C18600-TB00 vs C18600-TM06: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Shear Modulus 48 GPa7 Msi · Bulk Modulus 138 GPa20 Msi · Poisson's Ratio 0.34
Physical
Density and transition temperatures.
Same in both: Density 8.89 g/cm³0.32 lb/in³ · Melting Point (Solidus) 1,070°C1,958 °F · Liquidus Temperature 1,080°C1,976 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 385 J/kg·K0.09 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 17 µm/m·K9.4 µin/in·°F · Latent Heat of Fusion 205 J/g88.1 BTU/lb · Min Service Temperature -200°C-328 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.22 V · Corrosion Resistance 62 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Brazeability / Solderability 70 / 100 · Polishability 75 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 57 MJ/kg24,506 BTU/lb · Embodied Carbon (primary production) 3.6 kg CO₂/kg · Embodied Water 250 L/kg30 gal/lb · Typical Recycled Content 35%
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
C18600-TB00 vs C18600-TM06 — frequently asked
Is C18600-TM06 stronger than C18600-TB00?
Yes. C18600-TM06 has a typical yield strength of 560 MPa (81.2 ksi) against 95 MPa (13.8 ksi) for C18600-TB00 — about 5.9 times as much. Tensile strength is 590 MPa (85.6 ksi) vs 250 MPa (36.3 ksi).
Which condition does FabDigit quote by default, TB00 or TM06?
TM04 is the default C18600 condition in the FabDigit quote flow (neither TB00 nor TM06). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, C18600-TB00 or C18600-TM06?
C18600-TM06, by a small margin. Both rate poor for machinability — 22/100 against 15/100 for C18600-TB00; for welding the order is C18600-TB00 first (fair, 45/100) then C18600-TM06 (fair, 38/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in C18600-TB00 and C18600-TM06 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.