Copper Alloy C17510 vs QCr0.5
Copper Alloy · grade comparison
Copper Alloy C17510 and QCr0.5 are both copper alloy grades. QCr0.5 is the stronger of the two: yield strength 315 MPa (45.7 ksi) against 170 MPa (24.7 ksi) for C17510, about 85% more; tensile strength follows at 420 MPa (60.9 ksi) vs 310 MPa (45 ksi). In exchange, C17510 is the more ductile: elongation 25% versus 22% for QCr0.5, and QCr0.5 is harder (125 HB vs 70 HB). C17510 is stiffer (131 GPa vs 117 GPa) and QCr0.5 runs hotter in service (400°C vs 200°C continuous). On the shop floor, QCr0.5 machines more easily (fair vs poor), C17510 welds better (good vs poor), and QCr0.5 sits in a lower cost tier (high, $$$$) than C17510 (specialty, $$$$$).
C17510Choose it when the part is bent, formed or impact-loaded, or when it will be welded.
QCr0.5Choose it when strength drives the design, or when the part sees heat.
C17510 vs QCr0.5: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Max Service Temperature (continuous)
Latent Heat of Fusion
Same in both: Thermal Expansion (CTE, 20–100 °C) 17.6 µm/m·K9.8 µin/in·°F · Min Service Temperature -200°C-328 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Castability
Brazeability / Solderability
Polishability
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | C17510 | QCr0.5 |
|---|---|---|
| CNC machining | Yes | — |
| Sheet metal | Yes | — |
| Default condition | A | — |
| Relative cost | $$$$$ Specialty | $$$$ High |
| Min. machined wall | 0.8 mm | — |
| Best machined surface | Ra 1.6 µm | — |
| Chrome Plating | Yes | — |
| Electropolishing | Yes | — |
| Nickel Plating | Yes | — |
| Painting | Yes | — |
| Tin Plating | Yes | — |
They share 4 finishes: Copper Plating, Electroless Nickel (EN), Gold Plating, Silver Plating.
C17510 vs QCr0.5 — frequently asked
Is QCr0.5 stronger than C17510?
Yes. QCr0.5 has a typical yield strength of 315 MPa (45.7 ksi) against 170 MPa (24.7 ksi) for C17510 — about 85% more. Tensile strength is 420 MPa (60.9 ksi) vs 310 MPa (45 ksi).
Which is cheaper, C17510 or QCr0.5?
QCr0.5 is the lower-cost material: it sits in the high tier ($$$$) while C17510 is specialty ($$$$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, C17510 or QCr0.5?
QCr0.5. Its machinability rates fair (45/100) against poor (25/100) for C17510; for welding the order is C17510 first (good, 58/100) then QCr0.5 (poor, 30/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in C17510 and QCr0.5 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.