Copper Alloy C17410 vs C17510
Copper Alloy · grade comparison
Copper Alloy C17410 and C17510 are both copper alloy grades. C17410 is the stronger of the two: yield strength 690 MPa (100 ksi) against 170 MPa (24.7 ksi) for C17510, about 4.1 times as much; tensile strength follows at 725 MPa (105 ksi) vs 310 MPa (45 ksi). In exchange, C17510 is the more ductile: elongation 25% versus 10% for C17410, and C17410 is harder (215 HV vs 75 HV). C17410 is stiffer (138 GPa vs 131 GPa) and C17410 conducts heat better (205 W/m·K vs 105 W/m·K). On the shop floor, C17410 machines more easily (fair vs poor) and C17410 sits in a lower cost tier (high, $$$$) than C17510 (specialty, $$$$$).
C17410Choose it when strength drives the design, or when the part is machined in volume.
C17510Choose it when the part is bent, formed or impact-loaded.
C17410 vs C17510: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Rockwell B
Hardness, Vickers
Reduction in Area
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Same in both: Shear Modulus 53 GPa7.7 Msi · Bulk Modulus 115 GPa16.7 Msi · Poisson's Ratio 0.3
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Same in both: Liquidus Temperature 1,070°C1,958 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Latent Heat of Fusion
Same in both: Thermal Expansion (CTE, 20–100 °C) 17.6 µm/m·K9.8 µin/in·°F · Max Service Temperature (continuous) 200°C392 °F · Min Service Temperature -200°C-328 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.2 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Brazeability / Solderability
Same in both: Castability 45 / 100 · Polishability 80 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | C17410 | C17510 |
|---|---|---|
| CNC machining | — | Yes |
| Sheet metal | — | Yes |
| Default condition | — | A |
| Relative cost | $$$$ High | $$$$$ Specialty |
| Min. machined wall | — | 0.8 mm |
| Best machined surface | — | Ra 1.6 µm |
| Chrome Plating | — | Yes |
| Electropolishing | — | Yes |
| Nickel Plating | — | Yes |
| Painting | — | Yes |
| Tin Plating | — | Yes |
They share 4 finishes: Copper Plating, Electroless Nickel (EN), Gold Plating, Silver Plating.
C17410 vs C17510 — frequently asked
Is C17410 stronger than C17510?
Yes. C17410 has a typical yield strength of 690 MPa (100 ksi) against 170 MPa (24.7 ksi) for C17510 — about 4.1 times as much. Tensile strength is 725 MPa (105 ksi) vs 310 MPa (45 ksi).
Which is cheaper, C17410 or C17510?
C17410 is the lower-cost material: it sits in the high tier ($$$$) while C17510 is specialty ($$$$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, C17410 or C17510?
C17410. Its machinability rates fair (45/100) against poor (25/100) for C17510.
Ready to make it?
Upload a CAD file and FabDigit prices the part in C17410 and C17510 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.