Copper Alloy C17500-TD02 vs C17500-TH02
Copper Alloy · C17500 temper comparison
C17500-TD02 and C17500-TH02 are two conditions of the same copper alloy grade, C17500: TD02 (solution heat treated and cold worked, half hard) versus TH02 (TD02 and precipitation hardened). The chemistry is identical, so every difference below comes from the condition. C17500-TH02 is the stronger of the two: yield strength 690 MPa (100 ksi) against 415 MPa (60.2 ksi) for C17500-TD02, about 66% more; tensile strength follows at 790 MPa (115 ksi) vs 480 MPa (69.6 ksi). In exchange, C17500-TD02 is the more ductile: elongation 12% versus 8% for C17500-TH02, and C17500-TH02 is harder (235 HB vs 145 HB). C17500-TH02 is stiffer (138 GPa vs 130 GPa) and C17500-TH02 runs hotter in service (350°C vs 200°C continuous). On the shop floor, C17500-TH02 machines more easily (fair vs poor) and C17500-TD02 welds better (65 vs 55 out of 100).
C17500-TD02Choose it when the part is bent, formed or impact-loaded, or when it will be welded.
C17500-TH02Choose it when strength drives the design, or when the part sees heat.
C17500-TD02 vs C17500-TH02: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Rockwell C
Hardness, Vickers
Same in both: Shear Modulus 53 GPa7.7 Msi · Bulk Modulus 115 GPa16.7 Msi · Poisson's Ratio 0.3
Physical
Density and transition temperatures.
Same in both: Density 8.75 g/cm³0.32 lb/in³ · Melting Point (Solidus) 1,030°C1,886 °F · Liquidus Temperature 1,070°C1,958 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 419 J/kg·K0.1 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 17.6 µm/m·K9.8 µin/in·°F · Latent Heat of Fusion 205 J/g88.1 BTU/lb · Min Service Temperature -200°C-328 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.22 V · Corrosion Resistance 65 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Castability 55 / 100 · Brazeability / Solderability 65 / 100 · Polishability 80 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 95 MJ/kg40,843 BTU/lb · Embodied Carbon (primary production) 6.5 kg CO₂/kg · Embodied Water 300 L/kg35.9 gal/lb · Typical Recycled Content 30%
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
C17500-TD02 vs C17500-TH02 — frequently asked
Is C17500-TH02 stronger than C17500-TD02?
Yes. C17500-TH02 has a typical yield strength of 690 MPa (100 ksi) against 415 MPa (60.2 ksi) for C17500-TD02 — about 66% more. Tensile strength is 790 MPa (115 ksi) vs 480 MPa (69.6 ksi).
Which condition does FabDigit quote by default, TD02 or TH02?
TF00 is the default C17500 condition in the FabDigit quote flow (neither TD02 nor TH02). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, C17500-TD02 or C17500-TH02?
C17500-TH02. Its machinability rates fair (40/100) against poor (30/100) for C17500-TD02; for welding the order is C17500-TD02 first (good, 65/100) then C17500-TH02 (good, 55/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in C17500-TD02 and C17500-TH02 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.