Copper Alloy C17410 vs CuCrZr
Copper Alloy · grade comparison
Copper Alloy C17410 and CuCrZr are both copper alloy grades. C17410 is the stronger of the two: yield strength 690 MPa (100 ksi) against 350 MPa (50.8 ksi) for CuCrZr, about 97% more; tensile strength follows at 725 MPa (105 ksi) vs 430 MPa (62.4 ksi). In exchange, CuCrZr is the more ductile: elongation 22% versus 10% for C17410, and C17410 is harder (215 HV vs 140 HV). C17410 is stiffer (138 GPa vs 125 GPa) and CuCrZr runs hotter in service (450°C vs 200°C continuous). On the shop floor, CuCrZr sits in a lower cost tier (premium, $$$) than C17410 (high, $$$$).
C17410Choose it when strength drives the design.
CuCrZrChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
C17410 vs CuCrZr: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Rockwell B
Hardness, Vickers
Reduction in Area
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Same in both: Latent Heat of Fusion 205 J/g88.1 BTU/lb · Min Service Temperature -200°C-328 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Castability
Brazeability / Solderability
Polishability
Same in both: Machinability 45 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Typical Recycled Content
Same in both: Embodied Water 300 L/kg35.9 gal/lb
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | C17410 | CuCrZr |
|---|---|---|
| 3D printing | — | Yes |
| Default condition | — | Aged |
| Relative cost | $$$$ High | $$$ Premium |
| Min. machined wall | — | — |
| Best machined surface | — | — |
Both take the same 4 finishes: Copper Plating, Electroless Nickel (EN), Gold Plating, Silver Plating.
C17410 vs CuCrZr — frequently asked
Is C17410 stronger than CuCrZr?
Yes. C17410 has a typical yield strength of 690 MPa (100 ksi) against 350 MPa (50.8 ksi) for CuCrZr — about 97% more. Tensile strength is 725 MPa (105 ksi) vs 430 MPa (62.4 ksi).
Which is cheaper, C17410 or CuCrZr?
CuCrZr is the lower-cost material: it sits in the premium tier ($$$) while C17410 is high ($$$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which welds better, C17410 or CuCrZr?
C17410. Its weldability rates good (55/100) against fair (50/100) for CuCrZr.
Ready to make it?
Upload a CAD file and FabDigit prices the part in C17410 and CuCrZr side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.