Copper Alloy C15900-H02 vs C15900-H08
Copper Alloy · C15900 temper comparison
C15900-H02 and C15900-H08 are two conditions of the same copper alloy grade, C15900: H02 (half hard) versus H08 (spring hard). The chemistry is identical, so every difference below comes from the condition. C15900-H08 is the stronger of the two: yield strength 570 MPa (82.7 ksi) against 470 MPa (68.2 ksi) for C15900-H02, about 21% more; tensile strength follows at 610 MPa (88.5 ksi) vs 515 MPa (74.7 ksi). In exchange, C15900-H02 is the more ductile: elongation 14% versus 8% for C15900-H08, and C15900-H08 is harder (160 HB vs 138 HB). C15900-H02 runs hotter in service (500°C vs 450°C continuous).
C15900-H02Choose it when the part is bent, formed or impact-loaded, or when the part sees heat.
C15900-H08Choose it when strength drives the design.
C15900-H02 vs C15900-H08: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 130 GPa18.9 Msi · Shear Modulus 48 GPa7 Msi · Bulk Modulus 140 GPa20.3 Msi · Poisson's Ratio 0.33
Physical
Density and transition temperatures.
Same in both: Density 8.86 g/cm³0.32 lb/in³ · Melting Point (Solidus) 1,083°C1,981 °F · Liquidus Temperature 1,083°C1,981 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 380 J/kg·K0.09 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 16.6 µm/m·K9.2 µin/in·°F · Latent Heat of Fusion 205 J/g88.1 BTU/lb · Min Service Temperature -269°C-452 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.22 V · Corrosion Resistance 55 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Brazeability / Solderability 85 / 100 · Polishability 65 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 65 MJ/kg27,945 BTU/lb · Embodied Carbon (primary production) 4.2 kg CO₂/kg · Embodied Water 320 L/kg38.3 gal/lb · Typical Recycled Content 5%
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
C15900-H02 vs C15900-H08 — frequently asked
Is C15900-H08 stronger than C15900-H02?
Yes. C15900-H08 has a typical yield strength of 570 MPa (82.7 ksi) against 470 MPa (68.2 ksi) for C15900-H02 — about 21% more. Tensile strength is 610 MPa (88.5 ksi) vs 515 MPa (74.7 ksi).
Which condition does FabDigit quote by default, H02 or H08?
H04 is the default C15900 condition in the FabDigit quote flow (neither H02 nor H08). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, C15900-H02 or C15900-H08?
C15900-H02. Its machinability rates fair (36/100) against poor (30/100) for C15900-H08; for welding the order is C15900-H02 first (poor, 25/100) then C15900-H08 (poor, 20/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in C15900-H02 and C15900-H08 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.