Copper Alloy C15100-H04 vs C15100-H06
Copper Alloy · C15100 temper comparison
C15100-H04 and C15100-H06 are two conditions of the same copper alloy grade, C15100: H04 (full hard) versus H06 (extra hard). The chemistry is identical, so every difference below comes from the condition. C15100-H06 is the stronger of the two: yield strength 375 MPa (54.4 ksi) against 330 MPa (47.9 ksi) for C15100-H04, about 14% more; tensile strength follows at 400 MPa (58 ksi) vs 360 MPa (52.2 ksi). In exchange, C15100-H04 is the more ductile: elongation 6% versus 4% for C15100-H06, and C15100-H06 is harder (118 HB vs 105 HB).
C15100-H04Choose it when the part is bent, formed or impact-loaded.
C15100-H06Choose it when strength drives the design.
C15100-H04 vs C15100-H06: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 120 GPa17.4 Msi · Shear Modulus 45 GPa6.5 Msi · Bulk Modulus 140 GPa20.3 Msi · Poisson's Ratio 0.33
Physical
Density and transition temperatures.
Same in both: Density 8.89 g/cm³0.32 lb/in³ · Melting Point (Solidus) 1,080°C1,976 °F · Liquidus Temperature 1,085°C1,985 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Same in both: Specific Heat Capacity 385 J/kg·K0.09 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 17.6 µm/m·K9.8 µin/in·°F · Latent Heat of Fusion 205 J/g88.1 BTU/lb · Max Service Temperature (continuous) 450°C842 °F · Min Service Temperature -200°C-328 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.2 V · Corrosion Resistance 60 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Formability (cold)
Same in both: Machinability Rating (AISI 1212 = 100 %) 20% · Weldability 45 / 100 · Castability 45 / 100 · Brazeability / Solderability 70 / 100 · Polishability 70 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 55 MJ/kg23,646 BTU/lb · Embodied Carbon (primary production) 3.8 kg CO₂/kg · Embodied Water 250 L/kg30 gal/lb · Typical Recycled Content 25%
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
C15100-H04 vs C15100-H06 — frequently asked
Is C15100-H06 stronger than C15100-H04?
Yes. C15100-H06 has a typical yield strength of 375 MPa (54.4 ksi) against 330 MPa (47.9 ksi) for C15100-H04 — about 14% more. Tensile strength is 400 MPa (58 ksi) vs 360 MPa (52.2 ksi).
Which condition does FabDigit quote by default, H04 or H06?
H04 is the default C15100 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
When should I choose C15100-H04 over C15100-H06?
Pick C15100-H04 when the part is bent, formed or impact-loaded. Pick C15100-H06 when strength drives the design.
Ready to make it?