Copper Alloy C14200-H01 vs C14200-H02
Copper Alloy · C14200 temper comparison
C14200-H01 and C14200-H02 are two conditions of the same copper alloy grade, C14200: H01 (quarter hard) versus H02 (half hard). The chemistry is identical, so every difference below comes from the condition. C14200-H02 is the stronger of the two: yield strength 250 MPa (36.3 ksi) against 200 MPa (29 ksi) for C14200-H01, about 25% more; tensile strength follows at 295 MPa (42.8 ksi) vs 260 MPa (37.7 ksi). In exchange, C14200-H01 is the more ductile: elongation 25% versus 14% for C14200-H02, and C14200-H02 is harder (85 HB vs 70 HB).
C14200-H01Choose it when the part is bent, formed or impact-loaded.
C14200-H02Choose it when strength drives the design.
C14200-H01 vs C14200-H02: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 117 GPa17 Msi · Shear Modulus 44 GPa6.4 Msi · Bulk Modulus 140 GPa20.3 Msi · Poisson's Ratio 0.34
Physical
Density and transition temperatures.
Same in both: Density 8.94 g/cm³0.32 lb/in³ · Melting Point (Solidus) 1,065°C1,949 °F · Liquidus Temperature 1,083°C1,981 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 190 W/m·K110 BTU/hr·ft·°F · Specific Heat Capacity 385 J/kg·K0.09 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 17.7 µm/m·K9.8 µin/in·°F · Latent Heat of Fusion 205 J/g88.1 BTU/lb · Min Service Temperature -200°C-328 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 40 % IACS · Electrical Resistivity 4.3×10⁻⁸ Ω·m1.69 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.2 V · Corrosion Resistance 68 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Formability (cold)
Same in both: Machinability Rating (AISI 1212 = 100 %) 20% · Weldability 70 / 100 · Brazeability / Solderability 95 / 100 · Polishability 70 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 58 MJ/kg24,936 BTU/lb · Embodied Carbon (primary production) 3.8 kg CO₂/kg · Embodied Water 250 L/kg30 gal/lb · Typical Recycled Content 35%
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
C14200-H01 vs C14200-H02 — frequently asked
Is C14200-H02 stronger than C14200-H01?
Yes. C14200-H02 has a typical yield strength of 250 MPa (36.3 ksi) against 200 MPa (29 ksi) for C14200-H01 — about 25% more. Tensile strength is 295 MPa (42.8 ksi) vs 260 MPa (37.7 ksi).
Which condition does FabDigit quote by default, H01 or H02?
OS050 is the default C14200 condition in the FabDigit quote flow (neither H01 nor H02). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, C14200-H01 or C14200-H02?
C14200-H02, by a small margin. Both rate fair for machinability — 40/100 against 35/100 for C14200-H01.
Ready to make it?
Upload a CAD file and FabDigit prices the part in C14200-H01 and C14200-H02 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.