Copper Alloy C12200 vs C12600
Copper Alloy · grade comparison
Copper Alloy C12200 and C12600 are both copper alloy grades. C12600 is the stronger of the two: yield strength 310 MPa (45 ksi) against 76 MPa (11 ksi) for C12200, about 4.1 times as much; tensile strength follows at 345 MPa (50 ksi) vs 235 MPa (34.1 ksi). In exchange, C12200 is the more ductile: elongation 45% versus 6% for C12600, and C12600 is harder (95 HB vs 45 HB). C12200 runs hotter in service (200°C vs 150°C continuous) and C12600 conducts heat better (388 W/m·K vs 339 W/m·K). On the shop floor, C12600 machines more easily (30 vs 20 out of 100) and C12200 welds better (excellent vs fair).
C12200Choose it when the part is bent, formed or impact-loaded, or when the part sees heat.
C12600Choose it when strength drives the design, or when the part is machined in volume.
C12200 vs C12600: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Rockwell B
Same in both: Elastic (Young's) Modulus 117 GPa17 Msi · Shear Modulus 44 GPa6.4 Msi · Bulk Modulus 140 GPa20.3 Msi · Poisson's Ratio 0.34
Physical
Density and transition temperatures.
Melting Point (Solidus)
Same in both: Density 8.94 g/cm³0.32 lb/in³ · Liquidus Temperature 1,083°C1,981 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 385 J/kg·K0.09 BTU/lb·°F · Latent Heat of Fusion 205 J/g88.1 BTU/lb · Min Service Temperature -200°C-328 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Weldability
Formability (cold)
Brazeability / Solderability
Polishability
Same in both: Machinability Rating (AISI 1212 = 100 %) 20%
Sustainability
Primary-production footprint per kilogram.
Embodied Water
Typical Recycled Content
Same in both: Embodied Energy (primary production) 55 MJ/kg23,646 BTU/lb · Embodied Carbon (primary production) 3.8 kg CO₂/kg
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Same in both: Specific Stiffness (E / density) 13.1 MN·m/kg
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | C12200 | C12600 |
|---|---|---|
| CNC machining | Yes | — |
| Sheet metal | Yes | — |
| Default condition | O | — |
| Relative cost | $$$$ High | $$$$ High |
| Min. machined wall | 0.8 mm | — |
| Best machined surface | Ra 1.6 µm | — |
| Chrome Plating | Yes | — |
| Electropolishing | Yes | — |
| Nickel Plating | Yes | — |
| Painting | Yes | — |
| Tin Plating | Yes | — |
They share 4 finishes: Copper Plating, Electroless Nickel (EN), Gold Plating, Silver Plating.
C12200 vs C12600 — frequently asked
Is C12600 stronger than C12200?
Yes. C12600 has a typical yield strength of 310 MPa (45 ksi) against 76 MPa (11 ksi) for C12200 — about 4.1 times as much. Tensile strength is 345 MPa (50 ksi) vs 235 MPa (34.1 ksi).
Which is cheaper, C12200 or C12600?
Both sit in the same relative cost tier ($$$$, high); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which is easier to machine, C12200 or C12600?
C12600, by a small margin. Both rate poor for machinability — 30/100 against 20/100 for C12200; for welding the order is C12200 first (excellent, 85/100) then C12600 (fair, 35/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in C12200 and C12600 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.