Copper Alloy C1020-H08 vs C1020-M
Copper Alloy · C1020 temper comparison
C1020-H08 and C1020-M are two conditions of the same copper alloy grade, C1020: H08 (spring hard) versus M (thermomechanically controlled processed). The chemistry is identical, so every difference below comes from the condition. C1020-H08 is the stronger of the two: yield strength 315 MPa (45.7 ksi) against 70 MPa (10.2 ksi) for C1020-M, about 4.5 times as much; tensile strength follows at 345 MPa (50 ksi) vs 210 MPa (30.5 ksi). In exchange, C1020-M is the more ductile: elongation 40% versus 4% for C1020-H08, and C1020-H08 is harder (110 HB vs 45 HB). C1020-M runs hotter in service (200°C vs 100°C continuous). On the shop floor, C1020-H08 machines more easily (fair vs poor) and C1020-M welds better (very good vs good).
C1020-H08Choose it when strength drives the design, or when the part is machined in volume.
C1020-MChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
C1020-H08 vs C1020-M: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Vickers
Same in both: Shear Modulus 44 GPa6.4 Msi · Bulk Modulus 140 GPa20.3 Msi · Poisson's Ratio 0.34
Physical
Density and transition temperatures.
Same in both: Density 8.94 g/cm³0.32 lb/in³ · Melting Point (Solidus) 1,083°C1,981 °F · Liquidus Temperature 1,083°C1,981 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 385 J/kg·K0.09 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 17 µm/m·K9.4 µin/in·°F · Latent Heat of Fusion 205 J/g88.1 BTU/lb · Min Service Temperature -269°C-452 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.3 V · Corrosion Resistance 60 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Castability 40 / 100 · Brazeability / Solderability 95 / 100 · Polishability 85 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 57 MJ/kg24,506 BTU/lb · Embodied Carbon (primary production) 3.8 kg CO₂/kg · Embodied Water 250 L/kg30 gal/lb · Typical Recycled Content 25%
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
C1020-H08 vs C1020-M — frequently asked
Is C1020-H08 stronger than C1020-M?
Yes. C1020-H08 has a typical yield strength of 315 MPa (45.7 ksi) against 70 MPa (10.2 ksi) for C1020-M — about 4.5 times as much. Tensile strength is 345 MPa (50 ksi) vs 210 MPa (30.5 ksi).
Which condition does FabDigit quote by default, H08 or M?
O is the default C1020 condition in the FabDigit quote flow (neither H08 nor M). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, C1020-H08 or C1020-M?
C1020-H08. Its machinability rates fair (35/100) against poor (25/100) for C1020-M; for welding the order is C1020-M first (very good, 75/100) then C1020-H08 (good, 60/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in C1020-H08 and C1020-M side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.