5056 Aluminum Honeycomb vs XPS Foam Core
Composite · grade comparison
5056 Aluminum Honeycomb and XPS Foam Core are both composite grades. 5056 Aluminum Honeycomb is the stronger of the two: yield strength 3 MPa (0.493 ksi) against 0.36 MPa (0.0522 ksi) for XPS Foam Core, about 9.4 times as much; tensile strength follows at 4 MPa (0.624 ksi) vs 0.4 MPa (0.058 ksi). XPS Foam Core is lighter (0.03 g/cm³ vs 0.05 g/cm³ for 5056 Aluminum Honeycomb) and 5056 Aluminum Honeycomb is stiffer (1 GPa vs 0.01 GPa). On the shop floor, XPS Foam Core machines more easily (excellent vs fair) and XPS Foam Core sits in a lower cost tier (standard, $$) than 5056 Aluminum Honeycomb (high, $$$$).
5056 Aluminum HoneycombChoose it when strength drives the design, or when the part sees heat.
XPS Foam CoreChoose it when weight is the constraint, or when the part is machined in volume.
5056 Aluminum Honeycomb vs XPS Foam Core: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all composite grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all composite grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
5056 Aluminum HoneycombXPS Foam Core
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Compressive Strength
Compressive Modulus
Shear Strength
Poisson's Ratio
Elongation at Break
Flexural Strength
Flexural Modulus
Physical
Density and transition temperatures.
Density
Glass Transition (Tg)
Water Absorption (24 h)
Water Absorption (Saturation)
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Min Service Temperature
Limiting Oxygen Index
Max Service Temperature (short-term)
Electrical
Conductivity and insulation.
Electrical Resistivity
Dielectric Constant (1 MHz)
Volume Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
UV / Weathering Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Same in both: Typical Recycled Content 10%
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Thermal Diffusivity
Same in both: Modulus of Resilience 6 kJ/m³ · Thermal Shock Resistance Index 0
Strength versus weight
Yield strength against density for every composite grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 5056 Aluminum Honeycomb | XPS Foam Core |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$$$ High | $$ Standard |
| Min. machined wall | — | — |
| Best machined surface | — | — |
5056 Aluminum Honeycomb vs XPS Foam Core — frequently asked
Is 5056 Aluminum Honeycomb stronger than XPS Foam Core?
Yes. 5056 Aluminum Honeycomb has a typical yield strength of 3 MPa (0.493 ksi) against 0.36 MPa (0.0522 ksi) for XPS Foam Core — about 9.4 times as much. Tensile strength is 4 MPa (0.624 ksi) vs 0.4 MPa (0.058 ksi).
Which is cheaper, 5056 Aluminum Honeycomb or XPS Foam Core?
XPS Foam Core is the lower-cost material: it sits in the standard tier ($$) while 5056 Aluminum Honeycomb is high ($$$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, 5056 Aluminum Honeycomb or XPS Foam Core?
XPS Foam Core. Its machinability rates excellent (88/100) against fair (35/100) for 5056 Aluminum Honeycomb.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 5056 Aluminum Honeycomb and XPS Foam Core side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.