YG6 vs YT14
Ceramic · grade comparison
YG6 and YT14 are both ceramic grades. YG6 is the stronger of the two: tensile strength 1,100 MPa (160 ksi) against 850 MPa (123 ksi) for YT14, about 29% more. YG6 is the more ductile: elongation 0.2% versus 0.1% for YT14, and YG6 is harder (1,580 HV vs 1,400 HV). YT14 is lighter (11.4 g/cm³ vs 14.9 g/cm³ for YG6) and YG6 is stiffer (630 GPa vs 520 GPa).
YG6Choose it when strength drives the design, or when the part is bent, formed or impact-loaded.
YT14Choose it when weight is the constraint, or when the part sees heat.
YG6 vs YT14: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all ceramic grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all ceramic grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Tensile Strength (Ultimate)
Elongation at Break
Compressive Strength
Flexural Strength
Shear Strength
Fracture Toughness (K_IC)
Hardness, Vickers
Hardness, Knoop
Same in both: Poisson's Ratio 0.22 · Hardness, Mohs 9
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Porosity
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Min Service Temperature
Electrical
Conductivity and insulation.
Electrical Resistivity
Volume Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Polishability
Sintering / Firing Temperature
Same in both: Machinability 5 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every ceramic grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | YG6 | YT14 |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$$$ High | $$$$ High |
| Min. machined wall | — | — |
| Best machined surface | — | — |
YG6 vs YT14 — frequently asked
Is YG6 stronger than YT14?
Yes. YG6 has a typical tensile strength of 1,100 MPa (160 ksi) against 850 MPa (123 ksi) for YT14 — about 29% more.
Which is cheaper, YG6 or YT14?
Both sit in the same relative cost tier ($$$$, high); the part price will be decided by machining time, tolerance and quantity rather than by the material.
When should I choose YG6 over YT14?
Pick YG6 when strength drives the design, or when the part is bent, formed or impact-loaded. Pick YT14 when weight is the constraint, or when the part sees heat.
Ready to make it?
Upload a CAD file and FabDigit prices the part in YG6 and YT14 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.