YG6 vs YG8
Ceramic · grade comparison
YG6 and YG8 are both ceramic grades. YG8 is the stronger of the two: tensile strength 1,200 MPa (174 ksi) against 1,100 MPa (160 ksi) for YG6, about 9% more. In exchange, YG6 is the more ductile: elongation 0.2% versus 0.1% for YG8, and YG6 is harder (1,580 HV vs 1,350 HV).
YG6Choose it when the part is bent, formed or impact-loaded.
YG8Choose it when strength drives the design.
YG6 vs YG8: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all ceramic grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all ceramic grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Tensile Strength (Ultimate)
Elongation at Break
Compressive Strength
Flexural Strength
Shear Strength
Fracture Toughness (K_IC)
Hardness, Vickers
Hardness, Knoop
Same in both: Poisson's Ratio 0.22 · Hardness, Mohs 9
Physical
Density and transition temperatures.
Density
Same in both: Melting Point (Solidus) 1,320°C2,408 °F · Porosity 0.02%
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Thermal Expansion (CTE, 20–100 °C)
Min Service Temperature
Same in both: Specific Heat Capacity 220 J/kg·K0.05 BTU/lb·°F · Max Service Temperature (continuous) 600°C1,112 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Resistivity 2×10⁻⁷ Ω·m7.87 µΩ·in · Volume Resistivity 2×10⁻⁵ Ω·cm
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Same in both: Machinability 5 / 100 · Polishability 90 / 100 · Sintering / Firing Temperature 1,420°C2,588 °F
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Same in both: Embodied Water 400 L/kg47.9 gal/lb · Typical Recycled Content 30%
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Thermal Diffusivity
Same in both: Thermal Shock Resistance Index 31
Strength versus weight
Yield strength against density for every ceramic grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | YG6 | YG8 |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$$$ High | $$$$ High |
| Min. machined wall | — | — |
| Best machined surface | — | — |
YG6 vs YG8 — frequently asked
Is YG8 stronger than YG6?
Yes. YG8 has a typical tensile strength of 1,200 MPa (174 ksi) against 1,100 MPa (160 ksi) for YG6 — about 9% more.
Which is cheaper, YG6 or YG8?
Both sit in the same relative cost tier ($$$$, high); the part price will be decided by machining time, tolerance and quantity rather than by the material.
When should I choose YG6 over YG8?
Pick YG6 when the part is bent, formed or impact-loaded. Pick YG8 when strength drives the design.
Ready to make it?
Upload a CAD file and FabDigit prices the part in YG6 and YG8 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.