YG10 vs YG6
Ceramic · grade comparison
YG10 and YG6 are both ceramic grades. YG10 is the stronger of the two: tensile strength 1,300 MPa (189 ksi) against 1,100 MPa (160 ksi) for YG6, about 18% more. In exchange, YG6 is the more ductile: elongation 0.2% versus 0% for YG10, and YG6 is harder (1,580 HV vs 1,350 HV). YG6 is stiffer (630 GPa vs 570 GPa) and YG6 runs hotter in service (600°C vs 550°C continuous).
YG10Choose it when strength drives the design.
YG6Choose it when the part is bent, formed or impact-loaded, or when the part sees heat.
YG10 vs YG6: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all ceramic grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all ceramic grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Tensile Strength (Ultimate)
Elongation at Break
Compressive Strength
Flexural Strength
Shear Strength
Fracture Toughness (K_IC)
Hardness, Vickers
Hardness, Knoop
Same in both: Poisson's Ratio 0.22 · Hardness, Mohs 9
Physical
Density and transition temperatures.
Density
Porosity
Same in both: Melting Point (Solidus) 1,320°C2,408 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Min Service Temperature
Same in both: Specific Heat Capacity 220 J/kg·K0.05 BTU/lb·°F
Electrical
Conductivity and insulation.
Volume Resistivity
Same in both: Electrical Resistivity 2×10⁻⁷ Ω·m7.87 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Polishability
Same in both: Machinability 5 / 100 · Sintering / Firing Temperature 1,420°C2,588 °F
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Same in both: Typical Recycled Content 30%
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every ceramic grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | YG10 | YG6 |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$$$ High | $$$$ High |
| Min. machined wall | — | — |
| Best machined surface | — | — |
YG10 vs YG6 — frequently asked
Is YG10 stronger than YG6?
Yes. YG10 has a typical tensile strength of 1,300 MPa (189 ksi) against 1,100 MPa (160 ksi) for YG6 — about 18% more.
Which is cheaper, YG10 or YG6?
Both sit in the same relative cost tier ($$$$, high); the part price will be decided by machining time, tolerance and quantity rather than by the material.
When should I choose YG10 over YG6?
Pick YG10 when strength drives the design. Pick YG6 when the part is bent, formed or impact-loaded, or when the part sees heat.
Ready to make it?
Upload a CAD file and FabDigit prices the part in YG10 and YG6 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.