Aluminum ZL111-T1 vs ZL111-T5
Aluminum · ZL111 temper comparison
ZL111-T1 and ZL111-T5 are two conditions of the same aluminum grade, ZL111: T1 (cooled from hot working and naturally aged) versus T5 (cooled from hot working and artificially aged). The chemistry is identical, so every difference below comes from the condition. ZL111-T5 is the stronger of the two: yield strength 225 MPa (32.6 ksi) against 195 MPa (28.3 ksi) for ZL111-T1, about 15% more; tensile strength follows at 300 MPa (43.5 ksi) vs 265 MPa (38.4 ksi). ZL111-T5 is the more ductile: elongation 3% versus 1.8% for ZL111-T1, and ZL111-T5 is harder (95 HB vs 90 HB).
ZL111-T5Choose it when strength drives the design, or when the part is bent, formed or impact-loaded.
ZL111-T1 vs ZL111-T5: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Same in both: Elastic (Young's) Modulus 72 GPa10.4 Msi · Shear Modulus 27 GPa3.9 Msi · Bulk Modulus 71 GPa10.3 Msi · Poisson's Ratio 0.33
Physical
Density and transition temperatures.
Same in both: Density 2.73 g/cm³0.1 lb/in³ · Melting Point (Solidus) 525°C977 °F · Liquidus Temperature 600°C1,112 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Same in both: Specific Heat Capacity 963 J/kg·K0.23 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 21.5 µm/m·K11.9 µin/in·°F · Latent Heat of Fusion 430 J/g185 BTU/lb · Max Service Temperature (continuous) 150°C302 °F · Min Service Temperature -70°C-94 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.78 V · Corrosion Resistance 42 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Formability (cold)
Same in both: Weldability 40 / 100 · Castability 85 / 100 · Brazeability / Solderability 25 / 100 · Polishability 40 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 200 MJ/kg85,985 BTU/lb · Embodied Carbon (primary production) 12.5 kg CO₂/kg · Embodied Water 1,100 L/kg132 gal/lb · Typical Recycled Content 60%
Strength versus weight
Yield strength against density for every aluminum grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
ZL111-T1 vs ZL111-T5 — frequently asked
Is ZL111-T5 stronger than ZL111-T1?
Yes. ZL111-T5 has a typical yield strength of 225 MPa (32.6 ksi) against 195 MPa (28.3 ksi) for ZL111-T1 — about 15% more. Tensile strength is 300 MPa (43.5 ksi) vs 265 MPa (38.4 ksi).
Which condition does FabDigit quote by default, T1 or T5?
T6 is the default ZL111 condition in the FabDigit quote flow (neither T1 nor T5). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
When should I choose ZL111-T1 over ZL111-T5?
Pick ZL111-T5 when strength drives the design, or when the part is bent, formed or impact-loaded.
Ready to make it?
Upload a CAD file and FabDigit prices the part in ZL111-T1 and ZL111-T5 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.