Aluminum EN AC-48000-F vs EN AC-48000-T5
Aluminum · EN AC-48000 temper comparison
EN AC-48000-F and EN AC-48000-T5 are two conditions of the same aluminum grade, EN AC-48000: F (as fabricated) versus T5 (cooled from hot working and artificially aged). The chemistry is identical, so every difference below comes from the condition. EN AC-48000-T5 is the stronger of the two: yield strength 190 MPa (27.6 ksi) against 130 MPa (18.9 ksi) for EN AC-48000-F, about 46% more; tensile strength follows at 215 MPa (31.2 ksi) vs 180 MPa (26.1 ksi). In exchange, EN AC-48000-F is the more ductile: elongation 1.5% versus 1% for EN AC-48000-T5, and EN AC-48000-T5 is harder (100 HB vs 85 HB). EN AC-48000-T5 runs hotter in service (230°C vs 180°C continuous) and EN AC-48000-T5 conducts electricity better (35 % IACS vs 29 % IACS). On the shop floor, EN AC-48000-F machines more easily (good vs fair).
EN AC-48000-FChoose it when the part is bent, formed or impact-loaded, or when the part is machined in volume.
EN AC-48000-T5Choose it when strength drives the design, or when the part sees heat.
EN AC-48000-F vs EN AC-48000-T5: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fracture Toughness (K_IC)
Hardness, Brinell
Hardness, Vickers
Same in both: Poisson's Ratio 0.33 · Compressive Strength 480 MPa69.6 ksi · Fatigue Strength (Endurance Limit) 80 MPa11.6 ksi · Charpy V-Notch Impact (RT) 2 J1.5 ft·lbf
Physical
Density and transition temperatures.
Same in both: Density 2.7 g/cm³0.1 lb/in³ · Melting Point (Solidus) 510°C950 °F · Liquidus Temperature 570°C1,058 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 140 W/m·K80.9 BTU/hr·ft·°F · Specific Heat Capacity 880 J/kg·K0.21 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 19.5 µm/m·K10.8 µin/in·°F · Latent Heat of Fusion 490 J/g211 BTU/lb · Min Service Temperature -60°C-76 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.8 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Same in both: Formability (cold) 5 / 100 · Castability 85 / 100 · Brazeability / Solderability 20 / 100 · Polishability 40 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Typical Recycled Content
Same in both: Embodied Water 1,200 L/kg144 gal/lb
Strength versus weight
Yield strength against density for every aluminum grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
EN AC-48000-F vs EN AC-48000-T5 — frequently asked
Is EN AC-48000-T5 stronger than EN AC-48000-F?
Yes. EN AC-48000-T5 has a typical yield strength of 190 MPa (27.6 ksi) against 130 MPa (18.9 ksi) for EN AC-48000-F — about 46% more. Tensile strength is 215 MPa (31.2 ksi) vs 180 MPa (26.1 ksi).
Which condition does FabDigit quote by default, F or T5?
T6 is the default EN AC-48000 condition in the FabDigit quote flow (neither F nor T5). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, EN AC-48000-F or EN AC-48000-T5?
EN AC-48000-F. Its machinability rates good (58/100) against fair (45/100) for EN AC-48000-T5; for welding the order is EN AC-48000-T5 first (poor, 30/100) then EN AC-48000-F (poor, 25/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in EN AC-48000-F and EN AC-48000-T5 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.