Aluminum EN AC-46000 F-S vs EN AC-46000-T6
Aluminum · EN AC-46000 temper comparison
EN AC-46000 F-S and EN AC-46000-T6 are two conditions of the same aluminum grade, EN AC-46000: F-S (f) versus T6 (solution heat treated and artificially aged). The chemistry is identical, so every difference below comes from the condition. EN AC-46000-T6 is the stronger of the two: yield strength 240 MPa (34.8 ksi) against 95 MPa (13.8 ksi) for EN AC-46000 F-S, about 153% more; tensile strength follows at 300 MPa (43.5 ksi) vs 150 MPa (21.8 ksi). EN AC-46000-T6 is harder — 110 HB against 60 HB for EN AC-46000 F-S — which matters for wear surfaces and threads. EN AC-46000-T6 is stiffer (75 GPa vs 70 GPa) and EN AC-46000-T6 runs hotter in service (170°C vs 150°C continuous). On the shop floor, EN AC-46000 F-S welds better (fair vs poor).
EN AC-46000 F-SChoose it when it will be welded.
EN AC-46000-T6Choose it when strength drives the design, or when surface hardness matters.
EN AC-46000 F-S vs EN AC-46000-T6: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Shear Modulus 27 GPa3.9 Msi · Bulk Modulus 74 GPa10.7 Msi · Poisson's Ratio 0.33 · Elongation at Break 1%
Physical
Density and transition temperatures.
Same in both: Density 2.75 g/cm³0.1 lb/in³ · Melting Point (Solidus) 515°C959 °F · Liquidus Temperature 595°C1,103 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 963 J/kg·K0.23 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 21 µm/m·K11.7 µin/in·°F · Latent Heat of Fusion 389 J/g167 BTU/lb · Min Service Temperature -50°C-58 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.78 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Weldability
Same in both: Machinability 72 / 100 · Machinability Rating (AISI 1212 = 100 %) 75% · Formability (cold) 5 / 100 · Castability 95 / 100 · Brazeability / Solderability 20 / 100 · Polishability 40 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 200 MJ/kg85,985 BTU/lb · Embodied Carbon (primary production) 12 kg CO₂/kg · Embodied Water 1,100 L/kg132 gal/lb · Typical Recycled Content 90%
Strength versus weight
Yield strength against density for every aluminum grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
EN AC-46000 F-S vs EN AC-46000-T6 — frequently asked
Is EN AC-46000-T6 stronger than EN AC-46000 F-S?
Yes. EN AC-46000-T6 has a typical yield strength of 240 MPa (34.8 ksi) against 95 MPa (13.8 ksi) for EN AC-46000 F-S — about 153% more. Tensile strength is 300 MPa (43.5 ksi) vs 150 MPa (21.8 ksi).
Which condition does FabDigit quote by default, F-S or T6?
F-D is the default EN AC-46000 condition in the FabDigit quote flow (neither F-S nor T6). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which welds better, EN AC-46000 F-S or EN AC-46000-T6?
EN AC-46000 F-S. Its weldability rates fair (35/100) against poor (25/100) for EN AC-46000-T6.
Ready to make it?
Upload a CAD file and FabDigit prices the part in EN AC-46000 F-S and EN AC-46000-T6 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.