Aluminum B4C/6061-O vs B4C/6061-T6
Aluminum · B4C/6061 temper comparison
B4C/6061-O and B4C/6061-T6 are two conditions of the same aluminum grade, B4C/6061: O (annealed) versus T6 (solution heat treated and artificially aged). The chemistry is identical, so every difference below comes from the condition. B4C/6061-T6 is the stronger of the two: yield strength 300 MPa (43.5 ksi) against 85 MPa (12.3 ksi) for B4C/6061-O, about 3.5 times as much; tensile strength follows at 345 MPa (50 ksi) vs 165 MPa (23.9 ksi). In exchange, B4C/6061-O is the more ductile: elongation 12% versus 4.5% for B4C/6061-T6, and B4C/6061-T6 is harder (115 HB vs 48 HB). B4C/6061-O runs hotter in service (250°C vs 175°C continuous) and B4C/6061-O conducts electricity better (38 % IACS vs 32 % IACS).
B4C/6061-OChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
B4C/6061-T6Choose it when strength drives the design.
B4C/6061-O vs B4C/6061-T6: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 92 GPa13.3 Msi · Shear Modulus 35 GPa5.1 Msi · Bulk Modulus 82 GPa11.9 Msi · Poisson's Ratio 0.32
Physical
Density and transition temperatures.
Same in both: Density 2.67 g/cm³0.1 lb/in³ · Melting Point (Solidus) 582°C1,080 °F · Liquidus Temperature 652°C1,206 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 900 J/kg·K0.21 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 20.5 µm/m·K11.4 µin/in·°F · Latent Heat of Fusion 340 J/g146 BTU/lb · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.75 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Castability 30 / 100 · Brazeability / Solderability 30 / 100 · Polishability 40 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 235 MJ/kg101,032 BTU/lb · Embodied Carbon (primary production) 14 kg CO₂/kg · Embodied Water 1,200 L/kg144 gal/lb · Typical Recycled Content 5%
Strength versus weight
Yield strength against density for every aluminum grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
B4C/6061-O vs B4C/6061-T6 — frequently asked
Is B4C/6061-T6 stronger than B4C/6061-O?
Yes. B4C/6061-T6 has a typical yield strength of 300 MPa (43.5 ksi) against 85 MPa (12.3 ksi) for B4C/6061-O — about 3.5 times as much. Tensile strength is 345 MPa (50 ksi) vs 165 MPa (23.9 ksi).
Which condition does FabDigit quote by default, O or T6?
T651 is the default B4C/6061 condition in the FabDigit quote flow (neither O nor T6). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
When should I choose B4C/6061-O over B4C/6061-T6?
Pick B4C/6061-O when the part is bent, formed or impact-loaded, or when the part sees heat. Pick B4C/6061-T6 when strength drives the design.