Aluminum AlSi12 vs EN AC-47000
Aluminum · grade comparison
Aluminum AlSi12 and EN AC-47000 are both aluminum grades. AlSi12 is the stronger of the two: yield strength 250 MPa (36.3 ksi) against 140 MPa (20.3 ksi) for EN AC-47000, about 79% more; tensile strength follows at 400 MPa (58 ksi) vs 250 MPa (36.3 ksi). AlSi12 is the more ductile: elongation 5% versus 2% for EN AC-47000, and AlSi12 is harder (105 HB vs 70 HB). EN AC-47000 runs hotter in service (150°C vs 120°C continuous) and EN AC-47000 conducts electricity better (31 % IACS vs 27 % IACS). On the shop floor, AlSi12 welds better (very good vs fair) and EN AC-47000 sits in a lower cost tier (standard, $$) than AlSi12 (premium, $$$).
AlSi12Choose it when strength drives the design, or when the part is bent, formed or impact-loaded.
EN AC-47000Choose it when the part sees heat, or when cost is the deciding factor.
AlSi12 vs EN AC-47000: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Bulk Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Vickers
Same in both: Shear Modulus 27 GPa3.9 Msi · Poisson's Ratio 0.33 · Fracture Toughness (K_IC) 17 MPa·√m15.5 ksi·√in
Physical
Density and transition temperatures.
Density
Liquidus Temperature
Same in both: Melting Point (Solidus) 574°C1,065 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Latent Heat of Fusion
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 900 J/kg·K0.21 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 20.4 µm/m·K11.3 µin/in·°F · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.83 V · Corrosion Resistance 55 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Weldability
Formability (cold)
Brazeability / Solderability
Polishability
Machinability Rating (AISI 1212 = 100 %)
Same in both: Castability 95 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every aluminum grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | AlSi12 | EN AC-47000 |
|---|---|---|
| 3D printing | Yes | — |
| Default condition | As Printed | — |
| Relative cost | $$$ Premium | $$ Standard |
| Min. machined wall | — | — |
| Best machined surface | — | — |
| Anodized (Aluminum AM) | Yes | — |
| Plated (Metal AM) | Yes | — |
They share 4 finishes: Electroless Nickel (EN), Epoxy Coating, Gold Plating, Silver Plating.
AlSi12 vs EN AC-47000 — frequently asked
Is AlSi12 stronger than EN AC-47000?
Yes. AlSi12 has a typical yield strength of 250 MPa (36.3 ksi) against 140 MPa (20.3 ksi) for EN AC-47000 — about 79% more. Tensile strength is 400 MPa (58 ksi) vs 250 MPa (36.3 ksi).
Which is cheaper, AlSi12 or EN AC-47000?
EN AC-47000 is the lower-cost material: it sits in the standard tier ($$) while AlSi12 is premium ($$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, AlSi12 or EN AC-47000?
AlSi12, by a small margin. Both rate fair for machinability — 50/100 against 45/100 for EN AC-47000; for welding the order is AlSi12 first (very good, 80/100) then EN AC-47000 (fair, 45/100).