Aluminum AC9B-F vs AC9B-T7
Aluminum · AC9B temper comparison
AC9B-F and AC9B-T7 are two conditions of the same aluminum grade, AC9B: F (as fabricated) versus T7 (solution heat treated and overaged (stabilized)). The chemistry is identical, so every difference below comes from the condition. AC9B-T7 is the stronger of the two: yield strength 165 MPa (23.9 ksi) against 150 MPa (21.8 ksi) for AC9B-F, about 10% more; tensile strength follows at 185 MPa (26.8 ksi) vs 170 MPa (24.7 ksi). AC9B-T7 is the more ductile: elongation 0.8% versus 0.5% for AC9B-F, and AC9B-T7 is harder (110 HB vs 100 HB). AC9B-T7 runs hotter in service (280°C vs 180°C continuous).
AC9B-T7Choose it when strength drives the design, or when the part is bent, formed or impact-loaded.
AC9B-F vs AC9B-T7: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Same in both: Shear Modulus 31 GPa4.5 Msi · Bulk Modulus 76 GPa11 Msi · Poisson's Ratio 0.33
Physical
Density and transition temperatures.
Same in both: Density 2.68 g/cm³0.1 lb/in³ · Melting Point (Solidus) 507°C945 °F · Liquidus Temperature 670°C1,238 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 880 J/kg·K0.21 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 17.8 µm/m·K9.9 µin/in·°F · Latent Heat of Fusion 425 J/g183 BTU/lb · Min Service Temperature -80°C-112 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.8 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Weldability
Formability (cold)
Same in both: Machinability 30 / 100 · Machinability Rating (AISI 1212 = 100 %) 43% · Castability 70 / 100 · Brazeability / Solderability 20 / 100 · Polishability 45 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 155 MJ/kg66,638 BTU/lb · Embodied Carbon (primary production) 10.5 kg CO₂/kg · Embodied Water 1,100 L/kg132 gal/lb · Typical Recycled Content 55%
Strength versus weight
Yield strength against density for every aluminum grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
AC9B-F vs AC9B-T7 — frequently asked
Is AC9B-T7 stronger than AC9B-F?
Yes. AC9B-T7 has a typical yield strength of 165 MPa (23.9 ksi) against 150 MPa (21.8 ksi) for AC9B-F — about 10% more. Tensile strength is 185 MPa (26.8 ksi) vs 170 MPa (24.7 ksi).
Which condition does FabDigit quote by default, F or T7?
T6 is the default AC9B condition in the FabDigit quote flow (neither F nor T7). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
When should I choose AC9B-F over AC9B-T7?
Pick AC9B-T7 when strength drives the design, or when the part is bent, formed or impact-loaded.