Aluminum A201.0-T6 vs A201.0-T7
Aluminum · A201.0 temper comparison
A201.0-T6 and A201.0-T7 are two conditions of the same aluminum grade, A201.0: T6 (solution heat treated and artificially aged) versus T7 (solution heat treated and overaged (stabilized)). The chemistry is identical, so every difference below comes from the condition. A201.0-T6 is the stronger of the two: yield strength 435 MPa (63.1 ksi) against 379 MPa (55 ksi) for A201.0-T7, about 15% more; tensile strength follows at 483 MPa (70.1 ksi) vs 448 MPa (65 ksi). In exchange, A201.0-T7 is the more ductile: elongation 6% versus 5% for A201.0-T6, and A201.0-T6 is harder (140 HB vs 130 HB). A201.0-T7 runs hotter in service (200°C vs 150°C continuous).
A201.0-T6Choose it when strength drives the design.
A201.0-T7Choose it when the part is bent, formed or impact-loaded, or when the part sees heat.
A201.0-T6 vs A201.0-T7: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Hardness, Brinell
Same in both: Elastic (Young's) Modulus 71 GPa10.3 Msi · Shear Modulus 26.5 GPa3.8 Msi · Bulk Modulus 74 GPa10.7 Msi · Poisson's Ratio 0.33 · Compressive Strength 390 MPa56.6 ksi · Charpy V-Notch Impact (RT) 12 J8.9 ft·lbf
Physical
Density and transition temperatures.
Same in both: Density 2.8 g/cm³0.1 lb/in³ · Melting Point (Solidus) 571°C1,060 °F · Liquidus Temperature 650°C1,202 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 920 J/kg·K0.22 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 19.3 µm/m·K10.7 µin/in·°F · Latent Heat of Fusion 390 J/g168 BTU/lb · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Same in both: Electrical Resistivity 5.2×10⁻⁸ Ω·m2.05 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.69 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Same in both: Machinability Rating (AISI 1212 = 100 %) 130% · Weldability 40 / 100 · Formability (cold) 10 / 100 · Castability 30 / 100 · Brazeability / Solderability 15 / 100 · Polishability 55 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 205 MJ/kg88,134 BTU/lb · Embodied Carbon (primary production) 13 kg CO₂/kg · Embodied Water 1,150 L/kg138 gal/lb · Typical Recycled Content 5%
Strength versus weight
Yield strength against density for every aluminum grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
A201.0-T6 vs A201.0-T7 — frequently asked
Is A201.0-T6 stronger than A201.0-T7?
Yes. A201.0-T6 has a typical yield strength of 435 MPa (63.1 ksi) against 379 MPa (55 ksi) for A201.0-T7 — about 15% more. Tensile strength is 483 MPa (70.1 ksi) vs 448 MPa (65 ksi).
Which condition does FabDigit quote by default, T6 or T7?
T7 is the default A201.0 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
When should I choose A201.0-T6 over A201.0-T7?
Pick A201.0-T6 when strength drives the design. Pick A201.0-T7 when the part is bent, formed or impact-loaded, or when the part sees heat.
Ready to make it?
Upload a CAD file and FabDigit prices the part in A201.0-T6 and A201.0-T7 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.