Aluminum A201.0-F vs A201.0-T6
Aluminum · A201.0 temper comparison
A201.0-F and A201.0-T6 are two conditions of the same aluminum grade, A201.0: F (as fabricated) versus T6 (solution heat treated and artificially aged). The chemistry is identical, so every difference below comes from the condition. A201.0-T6 is the stronger of the two: yield strength 435 MPa (63.1 ksi) against 125 MPa (18.1 ksi) for A201.0-F, about 3.5 times as much; tensile strength follows at 483 MPa (70.1 ksi) vs 200 MPa (29 ksi). A201.0-T6 is the more ductile: elongation 5% versus 3% for A201.0-F, and A201.0-T6 is harder (140 HB vs 65 HB). On the shop floor, A201.0-T6 machines more easily (very good vs good).
A201.0-T6Choose it when strength drives the design, or when the part is bent, formed or impact-loaded.
A201.0-F vs A201.0-T6: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Same in both: Elastic (Young's) Modulus 71 GPa10.3 Msi · Shear Modulus 26.5 GPa3.8 Msi · Bulk Modulus 74 GPa10.7 Msi · Poisson's Ratio 0.33
Physical
Density and transition temperatures.
Same in both: Density 2.8 g/cm³0.1 lb/in³ · Melting Point (Solidus) 571°C1,060 °F · Liquidus Temperature 650°C1,202 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Same in both: Specific Heat Capacity 920 J/kg·K0.22 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 19.3 µm/m·K10.7 µin/in·°F · Latent Heat of Fusion 390 J/g168 BTU/lb · Max Service Temperature (continuous) 150°C302 °F · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Resistivity
Same in both: Electrical Conductivity 30 % IACS
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.69 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Castability 30 / 100 · Brazeability / Solderability 15 / 100 · Polishability 55 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 205 MJ/kg88,134 BTU/lb · Embodied Carbon (primary production) 13 kg CO₂/kg · Embodied Water 1,150 L/kg138 gal/lb · Typical Recycled Content 5%
Strength versus weight
Yield strength against density for every aluminum grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
A201.0-F vs A201.0-T6 — frequently asked
Is A201.0-T6 stronger than A201.0-F?
Yes. A201.0-T6 has a typical yield strength of 435 MPa (63.1 ksi) against 125 MPa (18.1 ksi) for A201.0-F — about 3.5 times as much. Tensile strength is 483 MPa (70.1 ksi) vs 200 MPa (29 ksi).
Which condition does FabDigit quote by default, F or T6?
T7 is the default A201.0 condition in the FabDigit quote flow (neither F nor T6). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, A201.0-F or A201.0-T6?
A201.0-T6. Its machinability rates very good (72/100) against good (60/100) for A201.0-F; for welding the order is A201.0-T6 first (fair, 40/100) then A201.0-F (fair, 35/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in A201.0-F and A201.0-T6 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.