Aluminum 8017-H16 vs 8017-H24
Aluminum · 8017 temper comparison
8017-H16 and 8017-H24 are two conditions of the same aluminum grade, 8017: H16 (strain hardened, three-quarter hard) versus H24 (strain hardened and partially annealed, half hard). The chemistry is identical, so every difference below comes from the condition. 8017-H16 is the stronger of the two: yield strength 130 MPa (18.9 ksi) against 105 MPa (15.2 ksi) for 8017-H24, about 24% more; tensile strength follows at 145 MPa (21 ksi) vs 125 MPa (18.1 ksi). In exchange, 8017-H24 is the more ductile: elongation 12% versus 6% for 8017-H16, and 8017-H16 is harder (42 HB vs 35 HB). 8017-H24 runs hotter in service (135°C vs 110°C continuous).
8017-H16Choose it when strength drives the design.
8017-H24Choose it when the part is bent, formed or impact-loaded, or when the part sees heat.
8017-H16 vs 8017-H24: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Same in both: Elastic (Young's) Modulus 69 GPa10 Msi · Shear Modulus 26 GPa3.8 Msi · Bulk Modulus 75 GPa10.9 Msi · Poisson's Ratio 0.33
Physical
Density and transition temperatures.
Same in both: Density 2.71 g/cm³0.1 lb/in³ · Melting Point (Solidus) 645°C1,193 °F · Liquidus Temperature 657°C1,215 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 900 J/kg·K0.21 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 23.6 µm/m·K13.1 µin/in·°F · Latent Heat of Fusion 397 J/g171 BTU/lb · Min Service Temperature -200°C-328 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.84 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Castability 45 / 100 · Brazeability / Solderability 55 / 100 · Polishability 50 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 200 MJ/kg85,985 BTU/lb · Embodied Carbon (primary production) 12 kg CO₂/kg · Embodied Water 1,100 L/kg132 gal/lb · Typical Recycled Content 20%
Strength versus weight
Yield strength against density for every aluminum grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
8017-H16 vs 8017-H24 — frequently asked
Is 8017-H16 stronger than 8017-H24?
Yes. 8017-H16 has a typical yield strength of 130 MPa (18.9 ksi) against 105 MPa (15.2 ksi) for 8017-H24 — about 24% more. Tensile strength is 145 MPa (21 ksi) vs 125 MPa (18.1 ksi).
Which condition does FabDigit quote by default, H16 or H24?
H12 is the default 8017 condition in the FabDigit quote flow (neither H16 nor H24). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 8017-H16 or 8017-H24?
8017-H16. Its machinability rates fair (35/100) against poor (30/100) for 8017-H24.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 8017-H16 and 8017-H24 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.