Aluminum 7A77 As Printed vs 7A77-T6
Aluminum · 7A77 temper comparison
7A77 As Printed and 7A77-T6 are two conditions of the same aluminum grade, 7A77: As Printed (as built (as printed)) versus T6 (solution heat treated and artificially aged). The chemistry is identical, so every difference below comes from the condition. 7A77-T6 is the stronger of the two: yield strength 480 MPa (69.6 ksi) against 310 MPa (45 ksi) for 7A77 As Printed, about 55% more; tensile strength follows at 545 MPa (79 ksi) vs 400 MPa (58 ksi). 7A77-T6 is harder — 150 HB against 110 HB for 7A77 As Printed — which matters for wear surfaces and threads. 7A77-T6 runs hotter in service (120°C vs 100°C continuous) and 7A77-T6 conducts heat better (130 W/m·K vs 105 W/m·K).
7A77-T6Choose it when strength drives the design, or when surface hardness matters.
7A77 As Printed vs 7A77-T6: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Hardness, Brinell
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 70 GPa10.2 Msi · Shear Modulus 26.5 GPa3.8 Msi · Bulk Modulus 69 GPa10 Msi · Poisson's Ratio 0.33 · Elongation at Break 5% · Charpy V-Notch Impact (RT) 6 J4.4 ft·lbf
Physical
Density and transition temperatures.
Same in both: Density 2.81 g/cm³0.1 lb/in³ · Melting Point (Solidus) 477°C891 °F · Liquidus Temperature 635°C1,175 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 960 J/kg·K0.23 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 23.4 µm/m·K13 µin/in·°F · Latent Heat of Fusion 390 J/g168 BTU/lb · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.83 V · Corrosion Resistance 40 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Same in both: Weldability 25 / 100 · Formability (cold) 20 / 100 · Castability 35 / 100 · Brazeability / Solderability 15 / 100 · Polishability 60 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 215 MJ/kg92,433 BTU/lb · Embodied Carbon (primary production) 13 kg CO₂/kg · Embodied Water 1,250 L/kg150 gal/lb · Typical Recycled Content 5%
Strength versus weight
Yield strength against density for every aluminum grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
7A77 As Printed vs 7A77-T6 — frequently asked
Is 7A77-T6 stronger than 7A77 As Printed?
Yes. 7A77-T6 has a typical yield strength of 480 MPa (69.6 ksi) against 310 MPa (45 ksi) for 7A77 As Printed — about 55% more. Tensile strength is 545 MPa (79 ksi) vs 400 MPa (58 ksi).
Which condition does FabDigit quote by default, As Printed or T6?
As Printed is the default 7A77 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 7A77 As Printed or 7A77-T6?
7A77-T6. Its machinability rates very good (72/100) against good (65/100) for 7A77 As Printed.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 7A77 As Printed and 7A77-T6 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.