Aluminum 7449-T651 vs 7449-T7651
Aluminum · 7449 temper comparison
7449-T651 and 7449-T7651 are two conditions of the same aluminum grade, 7449: T651 (T6, stress relieved by stretching) versus T7651 (T76, stress relieved by stretching). The chemistry is identical, so every difference below comes from the condition. Both yield at about 615 MPa — the mechanical properties are the same, and the difference is in how the stock is processed and what it is certified to (T6, stress relieved by stretching versus T76, stress relieved by stretching). 7449-T7651 is the more ductile: elongation 9% versus 8% for 7449-T651, and 7449-T651 is harder (205 HV vs 190 HV). 7449-T7651 runs hotter in service (120°C vs 100°C continuous) and 7449-T7651 conducts heat better (145 W/m·K vs 127 W/m·K).
7449-T7651Choose it when the part is bent, formed or impact-loaded, or when the part sees heat.
7449-T651 vs 7449-T7651: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Hardness, Brinell
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 70 GPa10.2 Msi · Shear Modulus 26.5 GPa3.8 Msi · Bulk Modulus 71 GPa10.3 Msi · Poisson's Ratio 0.33
Physical
Density and transition temperatures.
Same in both: Density 2.82 g/cm³0.1 lb/in³ · Melting Point (Solidus) 475°C887 °F · Liquidus Temperature 635°C1,175 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 860 J/kg·K0.21 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 23.4 µm/m·K13 µin/in·°F · Latent Heat of Fusion 390 J/g168 BTU/lb · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.83 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Weldability
Formability (cold)
Same in both: Machinability Rating (AISI 1212 = 100 %) 80% · Brazeability / Solderability 10 / 100 · Polishability 60 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 205 MJ/kg88,134 BTU/lb · Embodied Carbon (primary production) 12.5 kg CO₂/kg · Embodied Water 1,150 L/kg138 gal/lb · Typical Recycled Content 12%
Strength versus weight
Yield strength against density for every aluminum grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
7449-T651 vs 7449-T7651 — frequently asked
What is the difference between 7449-T651 and 7449-T7651?
7449-T651 and 7449-T7651 are two conditions of the same aluminum grade, 7449: T651 (T6, stress relieved by stretching) versus T7651 (T76, stress relieved by stretching). The chemistry is identical, so every difference below comes from the condition. Both yield at about 615 MPa — the mechanical properties are the same, and the difference is in how the stock is processed and what it is certified to (T6, stress relieved by stretching versus T76, stress relieved by stretching).
Which condition does FabDigit quote by default, T651 or T7651?
T7951 is the default 7449 condition in the FabDigit quote flow (neither T651 nor T7651). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
When should I choose 7449-T651 over 7449-T7651?
Pick 7449-T7651 when the part is bent, formed or impact-loaded, or when the part sees heat.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 7449-T651 and 7449-T7651 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.