Aluminum 6262-T6 vs 6262-T8
Aluminum · 6262 temper comparison
6262-T6 and 6262-T8 are two conditions of the same aluminum grade, 6262: T6 (solution heat treated and artificially aged) versus T8 (solution heat treated, cold worked and artificially aged). The chemistry is identical, so every difference below comes from the condition. 6262-T8 is the stronger of the two: yield strength 365 MPa (52.9 ksi) against 275 MPa (39.9 ksi) for 6262-T6, about 33% more; tensile strength follows at 395 MPa (57.3 ksi) vs 310 MPa (45 ksi). In exchange, 6262-T6 is the more ductile: elongation 12% versus 10% for 6262-T8, and 6262-T8 is harder (118 HB vs 95 HB).
6262-T6Choose it when the part is bent, formed or impact-loaded.
6262-T8Choose it when strength drives the design.
6262-T6 vs 6262-T8: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 69 GPa10 Msi · Shear Modulus 26 GPa3.8 Msi · Bulk Modulus 69 GPa10 Msi · Poisson's Ratio 0.33
Physical
Density and transition temperatures.
Same in both: Density 2.72 g/cm³0.1 lb/in³ · Melting Point (Solidus) 582°C1,080 °F · Liquidus Temperature 652°C1,206 °F
Thermal
How each material carries heat and how hot it can run.
Same in both: Thermal Conductivity 172 W/m·K99.4 BTU/hr·ft·°F · Specific Heat Capacity 895 J/kg·K0.21 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 23.4 µm/m·K13 µin/in·°F · Latent Heat of Fusion 393 J/g169 BTU/lb · Max Service Temperature (continuous) 150°C302 °F · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 44 % IACS · Electrical Resistivity 3.9×10⁻⁸ Ω·m1.54 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.8 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Brazeability / Solderability 30 / 100 · Polishability 60 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 200 MJ/kg85,985 BTU/lb · Embodied Carbon (primary production) 12 kg CO₂/kg · Embodied Water 1,200 L/kg144 gal/lb · Typical Recycled Content 25%
Strength versus weight
Yield strength against density for every aluminum grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
6262-T6 vs 6262-T8 — frequently asked
Is 6262-T8 stronger than 6262-T6?
Yes. 6262-T8 has a typical yield strength of 365 MPa (52.9 ksi) against 275 MPa (39.9 ksi) for 6262-T6 — about 33% more. Tensile strength is 395 MPa (57.3 ksi) vs 310 MPa (45 ksi).
Which condition does FabDigit quote by default, T6 or T8?
Specify the condition in the material field or the drawing note; FabDigit prices the quote for the state you call out.
Which welds better, 6262-T6 or 6262-T8?
6262-T6. Its weldability rates poor (30/100) against poor (25/100) for 6262-T8.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 6262-T6 and 6262-T8 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.