Aluminum 6111-O vs 6111-T4P
Aluminum · 6111 temper comparison
6111-O and 6111-T4P are two conditions of the same aluminum grade, 6111: O (annealed) versus T4P (solution treated, pre-aged (stabilised) for improved bake hardening). The chemistry is identical, so every difference below comes from the condition. 6111-T4P is the stronger of the two: yield strength 155 MPa (22.5 ksi) against 70 MPa (10.2 ksi) for 6111-O, about 121% more; tensile strength follows at 290 MPa (42.1 ksi) vs 150 MPa (21.8 ksi). In exchange, 6111-O is the more ductile: elongation 32% versus 27% for 6111-T4P, and 6111-T4P is harder (76 HB vs 42 HB). 6111-O runs hotter in service (200°C vs 120°C continuous) and 6111-O conducts heat better (190 W/m·K vs 167 W/m·K). On the shop floor, 6111-T4P machines more easily (good vs fair).
6111-OChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
6111-T4PChoose it when strength drives the design, or when the part is machined in volume.
6111-O vs 6111-T4P: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Hardness, Brinell
Same in both: Elastic (Young's) Modulus 70 GPa10.2 Msi · Shear Modulus 26 GPa3.8 Msi · Bulk Modulus 69 GPa10 Msi · Poisson's Ratio 0.33
Physical
Density and transition temperatures.
Same in both: Density 2.71 g/cm³0.1 lb/in³ · Melting Point (Solidus) 560°C1,040 °F · Liquidus Temperature 650°C1,202 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 895 J/kg·K0.21 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 23.5 µm/m·K13.1 µin/in·°F · Latent Heat of Fusion 390 J/g168 BTU/lb · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.74 V · Corrosion Resistance 58 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Formability (cold)
Same in both: Weldability 55 / 100 · Brazeability / Solderability 30 / 100 · Polishability 60 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 200 MJ/kg85,985 BTU/lb · Embodied Carbon (primary production) 12 kg CO₂/kg · Embodied Water 1,200 L/kg144 gal/lb · Typical Recycled Content 25%
Strength versus weight
Yield strength against density for every aluminum grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
6111-O vs 6111-T4P — frequently asked
Is 6111-T4P stronger than 6111-O?
Yes. 6111-T4P has a typical yield strength of 155 MPa (22.5 ksi) against 70 MPa (10.2 ksi) for 6111-O — about 121% more. Tensile strength is 290 MPa (42.1 ksi) vs 150 MPa (21.8 ksi).
Which condition does FabDigit quote by default, O or T4P?
T4 is the default 6111 condition in the FabDigit quote flow (neither O nor T4P). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 6111-O or 6111-T4P?
6111-T4P. Its machinability rates good (60/100) against fair (45/100) for 6111-O.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 6111-O and 6111-T4P side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.