Aluminum 6005A vs 6065
Aluminum · grade comparison
Aluminum 6005A and 6065 are both aluminum grades. 6065 is the stronger of the two: yield strength 375 MPa (54.4 ksi) against 235 MPa (34.1 ksi) for 6005A, about 60% more; tensile strength follows at 400 MPa (58 ksi) vs 275 MPa (39.9 ksi). 6065 is harder — 120 HB against 95 HB for 6005A — which matters for wear surfaces and threads. 6005A conducts electricity better (49 % IACS vs 44 % IACS). On the shop floor, 6065 machines more easily (excellent vs good), 6005A welds better (excellent vs fair), and 6005A forms better (fair vs poor).
6005AChoose it when it will be welded, or when cost is the deciding factor.
6065Choose it when strength drives the design, or when surface hardness matters.
6005A vs 6065: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Bulk Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Compressive Strength
Shear Strength
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Vickers
Same in both: Shear Modulus 26 GPa3.8 Msi · Poisson's Ratio 0.33 · Fatigue Strength (Endurance Limit) 90 MPa13.1 ksi · Fracture Toughness (K_IC) 29 MPa·√m26.4 ksi·√in
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Same in both: Latent Heat of Fusion 393 J/g169 BTU/lb · Max Service Temperature (continuous) 150°C302 °F · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Same in both: Corrosion Resistance 68 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Castability
Brazeability / Solderability
Polishability
Sustainability
Primary-production footprint per kilogram.
Embodied Carbon (primary production)
Typical Recycled Content
Same in both: Embodied Energy (primary production) 200 MJ/kg85,985 BTU/lb · Embodied Water 1,200 L/kg144 gal/lb
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every aluminum grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 6005A | 6065 |
|---|---|---|
| CNC machining | Yes | — |
| Sheet metal | Yes | — |
| Default condition | — | — |
| Relative cost | $ Budget | $$$ Premium |
| Min. machined wall | 0.5 mm | — |
| Best machined surface | Ra 0.8 µm | — |
| Anodizing Type II | Yes | — |
| Cerakote | Yes | — |
| Chem Film (Alodine) | Yes | — |
| DLC | Yes | — |
| E-Coating | Yes | — |
| Electropolishing | Yes | — |
| Hard Anodize Type III w/ PTFE | Yes | — |
| Hard Anodizing Type III | Yes | — |
| Nickel Plating | Yes | — |
| PTFE Coating | Yes | — |
| Painting | Yes | — |
| Powder Coating | Yes | — |
They share 4 finishes: Electroless Nickel (EN), Epoxy Coating, Gold Plating, Silver Plating.
6005A vs 6065 — frequently asked
Is 6065 stronger than 6005A?
Yes. 6065 has a typical yield strength of 375 MPa (54.4 ksi) against 235 MPa (34.1 ksi) for 6005A — about 60% more. Tensile strength is 400 MPa (58 ksi) vs 275 MPa (39.9 ksi).
Which is cheaper, 6005A or 6065?
6005A is the lower-cost material: it sits in the budget tier ($) while 6065 is premium ($$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, 6005A or 6065?
6065. Its machinability rates excellent (88/100) against good (62/100) for 6005A; for welding the order is 6005A first (excellent, 85/100) then 6065 (fair, 35/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 6005A and 6065 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.