Aluminum 6005A-T4 vs 6005A-T6
Aluminum · 6005A temper comparison
6005A-T4 and 6005A-T6 are two conditions of the same aluminum grade, 6005A: T4 (solution heat treated and naturally aged) versus T6 (solution heat treated and artificially aged). The chemistry is identical, so every difference below comes from the condition. 6005A-T6 is the stronger of the two: yield strength 235 MPa (34.1 ksi) against 110 MPa (16 ksi) for 6005A-T4, about 114% more; tensile strength follows at 275 MPa (39.9 ksi) vs 205 MPa (29.7 ksi). In exchange, 6005A-T4 is the more ductile: elongation 18% versus 11% for 6005A-T6, and 6005A-T6 is harder (95 HB vs 60 HB). 6005A-T6 runs hotter in service (150°C vs 100°C continuous) and 6005A-T6 conducts electricity better (49 % IACS vs 43 % IACS). On the shop floor, 6005A-T6 machines more easily (good vs fair).
6005A-T4Choose it when the part is bent, formed or impact-loaded.
6005A-T6Choose it when strength drives the design, or when the part sees heat.
6005A-T4 vs 6005A-T6: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 69.5 GPa10.1 Msi · Shear Modulus 26 GPa3.8 Msi · Bulk Modulus 69 GPa10 Msi · Poisson's Ratio 0.33
Physical
Density and transition temperatures.
Same in both: Density 2.7 g/cm³0.1 lb/in³ · Melting Point (Solidus) 607°C1,125 °F · Liquidus Temperature 654°C1,209 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 897 J/kg·K0.21 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 23 µm/m·K12.8 µin/in·°F · Latent Heat of Fusion 393 J/g169 BTU/lb · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.78 V · Corrosion Resistance 68 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Castability 25 / 100 · Brazeability / Solderability 45 / 100 · Polishability 70 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 200 MJ/kg85,985 BTU/lb · Embodied Carbon (primary production) 12.5 kg CO₂/kg · Embodied Water 1,200 L/kg144 gal/lb · Typical Recycled Content 30%
Strength versus weight
Yield strength against density for every aluminum grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
6005A-T4 vs 6005A-T6 — frequently asked
Is 6005A-T6 stronger than 6005A-T4?
Yes. 6005A-T6 has a typical yield strength of 235 MPa (34.1 ksi) against 110 MPa (16 ksi) for 6005A-T4 — about 114% more. Tensile strength is 275 MPa (39.9 ksi) vs 205 MPa (29.7 ksi).
Which condition does FabDigit quote by default, T4 or T6?
Specify the condition in the material field or the drawing note; FabDigit prices the quote for the state you call out.
Which is easier to machine, 6005A-T4 or 6005A-T6?
6005A-T6. Its machinability rates good (62/100) against fair (45/100) for 6005A-T4.