Aluminum 5A02-H112 vs 5A02-H14
Aluminum · 5A02 temper comparison
5A02-H112 and 5A02-H14 are two conditions of the same aluminum grade, 5A02: H112 (strain hardened from hot working only) versus H14 (strain hardened, half hard). The chemistry is identical, so every difference below comes from the condition. 5A02-H14 is the stronger of the two: yield strength 180 MPa (26.1 ksi) against 90 MPa (13.1 ksi) for 5A02-H112, about 100% more; tensile strength follows at 235 MPa (34.1 ksi) vs 185 MPa (26.8 ksi). In exchange, 5A02-H112 is the more ductile: elongation 16% versus 9% for 5A02-H14, and 5A02-H14 is harder (63 HB vs 50 HB). 5A02-H112 runs hotter in service (120°C vs 90°C continuous). On the shop floor, 5A02-H14 machines more easily (fair vs poor).
5A02-H112Choose it when the part is bent, formed or impact-loaded, or when the part sees heat.
5A02-H14Choose it when strength drives the design, or when the part is machined in volume.
5A02-H112 vs 5A02-H14: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Same in both: Elastic (Young's) Modulus 70 GPa10.2 Msi · Shear Modulus 26 GPa3.8 Msi · Bulk Modulus 69 GPa10 Msi · Poisson's Ratio 0.33
Physical
Density and transition temperatures.
Same in both: Density 2.68 g/cm³0.1 lb/in³ · Melting Point (Solidus) 607°C1,125 °F · Liquidus Temperature 650°C1,202 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 138 W/m·K79.7 BTU/hr·ft·°F · Specific Heat Capacity 900 J/kg·K0.21 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 23.8 µm/m·K13.2 µin/in·°F · Latent Heat of Fusion 395 J/g170 BTU/lb · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 35 % IACS · Electrical Resistivity 4.9×10⁻⁸ Ω·m1.93 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.86 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Formability (cold)
Same in both: Weldability 85 / 100 · Castability 25 / 100 · Brazeability / Solderability 25 / 100 · Polishability 65 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 200 MJ/kg85,985 BTU/lb · Embodied Carbon (primary production) 12.5 kg CO₂/kg · Embodied Water 1,100 L/kg132 gal/lb · Typical Recycled Content 30%
Strength versus weight
Yield strength against density for every aluminum grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
5A02-H112 vs 5A02-H14 — frequently asked
Is 5A02-H14 stronger than 5A02-H112?
Yes. 5A02-H14 has a typical yield strength of 180 MPa (26.1 ksi) against 90 MPa (13.1 ksi) for 5A02-H112 — about 100% more. Tensile strength is 235 MPa (34.1 ksi) vs 185 MPa (26.8 ksi).
Which condition does FabDigit quote by default, H112 or H14?
O is the default 5A02 condition in the FabDigit quote flow (neither H112 nor H14). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 5A02-H112 or 5A02-H14?
5A02-H14. Its machinability rates fair (42/100) against poor (32/100) for 5A02-H112.
Ready to make it?