Aluminum 5005-H112 vs 5005-H34
Aluminum · 5005 temper comparison
5005-H112 and 5005-H34 are two conditions of the same aluminum grade, 5005: H112 (strain hardened from hot working only) versus H34 (strain hardened and stabilized, half hard). The chemistry is identical, so every difference below comes from the condition. 5005-H34 is the stronger of the two: yield strength 138 MPa (20 ksi) against 60 MPa (8.7 ksi) for 5005-H112, about 130% more; tensile strength follows at 159 MPa (23.1 ksi) vs 130 MPa (18.9 ksi). In exchange, 5005-H112 is the more ductile: elongation 18% versus 8% for 5005-H34, and 5005-H34 is harder (41 HB vs 30 HB). 5005-H112 runs hotter in service (150°C vs 120°C continuous).
5005-H112Choose it when the part is bent, formed or impact-loaded, or when the part sees heat.
5005-H34Choose it when strength drives the design.
5005-H112 vs 5005-H34: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Same in both: Elastic (Young's) Modulus 68.9 GPa10 Msi · Shear Modulus 25.9 GPa3.8 Msi · Bulk Modulus 69 GPa10 Msi · Poisson's Ratio 0.33
Physical
Density and transition temperatures.
Same in both: Density 2.7 g/cm³0.1 lb/in³ · Melting Point (Solidus) 632°C1,170 °F · Liquidus Temperature 654°C1,209 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 900 J/kg·K0.21 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 23.8 µm/m·K13.2 µin/in·°F · Latent Heat of Fusion 397 J/g171 BTU/lb · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 52 % IACS · Electrical Resistivity 3.3×10⁻⁸ Ω·m1.3 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.83 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Brazeability / Solderability 45 / 100 · Polishability 72 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 205 MJ/kg88,134 BTU/lb · Embodied Carbon (primary production) 12 kg CO₂/kg · Embodied Water 1,150 L/kg138 gal/lb · Typical Recycled Content 35%
Strength versus weight
Yield strength against density for every aluminum grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
5005-H112 vs 5005-H34 — frequently asked
Is 5005-H34 stronger than 5005-H112?
Yes. 5005-H34 has a typical yield strength of 138 MPa (20 ksi) against 60 MPa (8.7 ksi) for 5005-H112 — about 130% more. Tensile strength is 159 MPa (23.1 ksi) vs 130 MPa (18.9 ksi).
Which condition does FabDigit quote by default, H112 or H34?
Specify the condition in the material field or the drawing note; FabDigit prices the quote for the state you call out.
Which is easier to machine, 5005-H112 or 5005-H34?
5005-H34, by a small margin. Both rate fair for machinability — 45/100 against 38/100 for 5005-H112.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 5005-H112 and 5005-H34 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.