Aluminum 4343-H14 vs 4343-H18
Aluminum · 4343 temper comparison
4343-H14 and 4343-H18 are two conditions of the same aluminum grade, 4343: H14 (strain hardened, half hard) versus H18 (strain hardened, full hard). The chemistry is identical, so every difference below comes from the condition. 4343-H18 is the stronger of the two: yield strength 200 MPa (29 ksi) against 165 MPa (23.9 ksi) for 4343-H14, about 21% more; tensile strength follows at 215 MPa (31.2 ksi) vs 185 MPa (26.8 ksi). In exchange, 4343-H14 is the more ductile: elongation 4% versus 2% for 4343-H18, and 4343-H18 is harder (58 HB vs 52 HB). 4343-H14 runs hotter in service (120°C vs 100°C continuous).
4343-H14Choose it when the part is bent, formed or impact-loaded, or when the part sees heat.
4343-H18Choose it when strength drives the design.
4343-H14 vs 4343-H18: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Same in both: Elastic (Young's) Modulus 69 GPa10 Msi · Shear Modulus 26 GPa3.8 Msi · Bulk Modulus 70 GPa10.2 Msi · Poisson's Ratio 0.33
Physical
Density and transition temperatures.
Same in both: Density 2.68 g/cm³0.1 lb/in³ · Melting Point (Solidus) 577°C1,071 °F · Liquidus Temperature 613°C1,135 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 178 W/m·K103 BTU/hr·ft·°F · Specific Heat Capacity 900 J/kg·K0.21 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 21.6 µm/m·K12 µin/in·°F · Latent Heat of Fusion 395 J/g170 BTU/lb · Min Service Temperature -269°C-452 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 41 % IACS · Electrical Resistivity 4.2×10⁻⁸ Ω·m1.65 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.81 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Castability 75 / 100 · Brazeability / Solderability 98 / 100 · Polishability 45 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 200 MJ/kg85,985 BTU/lb · Embodied Carbon (primary production) 12 kg CO₂/kg · Embodied Water 1,200 L/kg144 gal/lb · Typical Recycled Content 25%
Strength versus weight
Yield strength against density for every aluminum grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
4343-H14 vs 4343-H18 — frequently asked
Is 4343-H18 stronger than 4343-H14?
Yes. 4343-H18 has a typical yield strength of 200 MPa (29 ksi) against 165 MPa (23.9 ksi) for 4343-H14 — about 21% more. Tensile strength is 215 MPa (31.2 ksi) vs 185 MPa (26.8 ksi).
Which condition does FabDigit quote by default, H14 or H18?
Specify the condition in the material field or the drawing note; FabDigit prices the quote for the state you call out.
When should I choose 4343-H14 over 4343-H18?
Pick 4343-H14 when the part is bent, formed or impact-loaded, or when the part sees heat. Pick 4343-H18 when strength drives the design.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 4343-H14 and 4343-H18 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.