Aluminum 392.0-T6 vs 392.0-T7
Aluminum · 392.0 temper comparison
392.0-T6 and 392.0-T7 are two conditions of the same aluminum grade, 392.0: T6 (solution heat treated and artificially aged) versus T7 (solution heat treated and overaged (stabilized)). The chemistry is identical, so every difference below comes from the condition. 392.0-T6 is the stronger of the two: yield strength 310 MPa (45 ksi) against 260 MPa (37.7 ksi) for 392.0-T7, about 19% more; tensile strength follows at 330 MPa (47.9 ksi) vs 285 MPa (41.3 ksi). In exchange, 392.0-T7 is the more ductile: elongation 0.8% versus 0.5% for 392.0-T6, and 392.0-T6 is harder (125 HB vs 105 HB). 392.0-T7 runs hotter in service (250°C vs 200°C continuous) and 392.0-T7 conducts electricity better (28 % IACS vs 25 % IACS).
392.0-T6Choose it when strength drives the design.
392.0-T7Choose it when the part is bent, formed or impact-loaded, or when the part sees heat.
392.0-T6 vs 392.0-T7: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 82 GPa11.9 Msi · Shear Modulus 31 GPa4.5 Msi · Bulk Modulus 76 GPa11 Msi · Poisson's Ratio 0.33
Physical
Density and transition temperatures.
Same in both: Density 2.64 g/cm³0.1 lb/in³ · Melting Point (Solidus) 574°C1,065 °F · Liquidus Temperature 649°C1,200 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 963 J/kg·K0.23 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 17.8 µm/m·K9.9 µin/in·°F · Latent Heat of Fusion 425 J/g183 BTU/lb · Min Service Temperature -195°C-319 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.83 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Weldability
Formability (cold)
Same in both: Machinability 28 / 100 · Machinability Rating (AISI 1212 = 100 %) 33% · Castability 75 / 100 · Brazeability / Solderability 20 / 100 · Polishability 40 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 200 MJ/kg85,985 BTU/lb · Embodied Carbon (primary production) 12 kg CO₂/kg · Embodied Water 1,100 L/kg132 gal/lb · Typical Recycled Content 70%
Strength versus weight
Yield strength against density for every aluminum grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
392.0-T6 vs 392.0-T7 — frequently asked
Is 392.0-T6 stronger than 392.0-T7?
Yes. 392.0-T6 has a typical yield strength of 310 MPa (45 ksi) against 260 MPa (37.7 ksi) for 392.0-T7 — about 19% more. Tensile strength is 330 MPa (47.9 ksi) vs 285 MPa (41.3 ksi).
Which condition does FabDigit quote by default, T6 or T7?
F is the default 392.0 condition in the FabDigit quote flow (neither T6 nor T7). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
When should I choose 392.0-T6 over 392.0-T7?
Pick 392.0-T6 when strength drives the design. Pick 392.0-T7 when the part is bent, formed or impact-loaded, or when the part sees heat.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 392.0-T6 and 392.0-T7 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.