Aluminum 3104-H32 vs 3104-H34
Aluminum · 3104 temper comparison
3104-H32 and 3104-H34 are two conditions of the same aluminum grade, 3104: H32 (strain hardened and stabilized, quarter hard) versus H34 (strain hardened and stabilized, half hard). The chemistry is identical, so every difference below comes from the condition. 3104-H34 is the stronger of the two: yield strength 200 MPa (29 ksi) against 170 MPa (24.7 ksi) for 3104-H32, about 18% more; tensile strength follows at 240 MPa (34.8 ksi) vs 215 MPa (31.2 ksi). In exchange, 3104-H32 is the more ductile: elongation 14% versus 10% for 3104-H34, and 3104-H34 is harder (63 HB vs 52 HB).
3104-H32Choose it when the part is bent, formed or impact-loaded.
3104-H34Choose it when strength drives the design.
3104-H32 vs 3104-H34: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Hardness, Brinell
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 69 GPa10 Msi · Shear Modulus 26 GPa3.8 Msi · Bulk Modulus 69 GPa10 Msi · Poisson's Ratio 0.33 · Fatigue Strength (Endurance Limit) 105 MPa15.2 ksi
Physical
Density and transition temperatures.
Same in both: Density 2.72 g/cm³0.1 lb/in³ · Melting Point (Solidus) 629°C1,164 °F · Liquidus Temperature 654°C1,209 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Same in both: Specific Heat Capacity 893 J/kg·K0.21 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 23.2 µm/m·K12.9 µin/in·°F · Latent Heat of Fusion 396 J/g170 BTU/lb · Max Service Temperature (continuous) 125°C257 °F · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 42 % IACS · Electrical Resistivity 4.1×10⁻⁸ Ω·m1.61 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.83 V · Corrosion Resistance 70 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Formability (cold)
Same in both: Weldability 85 / 100 · Castability 30 / 100 · Brazeability / Solderability 35 / 100 · Polishability 50 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 200 MJ/kg85,985 BTU/lb · Embodied Carbon (primary production) 12.5 kg CO₂/kg · Embodied Water 1,150 L/kg138 gal/lb · Typical Recycled Content 70%
Strength versus weight
Yield strength against density for every aluminum grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
3104-H32 vs 3104-H34 — frequently asked
Is 3104-H34 stronger than 3104-H32?
Yes. 3104-H34 has a typical yield strength of 200 MPa (29 ksi) against 170 MPa (24.7 ksi) for 3104-H32 — about 18% more. Tensile strength is 240 MPa (34.8 ksi) vs 215 MPa (31.2 ksi).
Which condition does FabDigit quote by default, H32 or H34?
Specify the condition in the material field or the drawing note; FabDigit prices the quote for the state you call out.
When should I choose 3104-H32 over 3104-H34?
Pick 3104-H32 when the part is bent, formed or impact-loaded. Pick 3104-H34 when strength drives the design.