2A70-F and 2A70-T652 are two conditions of the same aluminum grade, 2A70: F (as fabricated) versus T652 (T6, stress relieved by compression). The chemistry is identical, so every difference below comes from the condition. 2A70-T652 is the stronger of the two: yield strength 345 MPa (50 ksi) against 160 MPa (23.2 ksi) for 2A70-F, about 116% more; tensile strength follows at 420 MPa (60.9 ksi) vs 280 MPa (40.6 ksi). In exchange, 2A70-F is the more ductile: elongation 15% versus 9% for 2A70-T652, and 2A70-T652 is harder (118 HB vs 80 HB). 2A70-T652 runs hotter in service (200°C vs 150°C continuous). On the shop floor, 2A70-T652 machines more easily (very good vs good).
2A70-FChoose it when the part is bent, formed or impact-loaded.
2A70-T652Choose it when strength drives the design, or when the part sees heat.
2A70-F vs 2A70-T652: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Vickers
Same in both: Shear Modulus 27.5 GPa4 Msi · Bulk Modulus 71 GPa10.3 Msi · Poisson's Ratio 0.33
Physical
Density and transition temperatures.
Same in both: Density 2.8 g/cm³0.1 lb/in³ · Melting Point (Solidus) 505°C941 °F · Liquidus Temperature 638°C1,180 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 875 J/kg·K0.21 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 22.3 µm/m·K12.4 µin/in·°F · Latent Heat of Fusion 390 J/g168 BTU/lb · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.68 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Castability 35 / 100 · Brazeability / Solderability 15 / 100 · Polishability 55 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 200 MJ/kg85,985 BTU/lb · Embodied Carbon (primary production) 12.5 kg CO₂/kg · Embodied Water 1,150 L/kg138 gal/lb · Typical Recycled Content 10%
Strength versus weight
Yield strength against density for every aluminum grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
2A70-F vs 2A70-T652 — frequently asked
Is 2A70-T652 stronger than 2A70-F?
Yes. 2A70-T652 has a typical yield strength of 345 MPa (50 ksi) against 160 MPa (23.2 ksi) for 2A70-F — about 116% more. Tensile strength is 420 MPa (60.9 ksi) vs 280 MPa (40.6 ksi).
Which condition does FabDigit quote by default, F or T652?
T6 is the default 2A70 condition in the FabDigit quote flow (neither F nor T652). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 2A70-F or 2A70-T652?
2A70-T652. Its machinability rates very good (72/100) against good (55/100) for 2A70-F.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 2A70-F and 2A70-T652 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.