Aluminum 2A25-O vs 2A25-T651
Aluminum · 2A25 temper comparison
2A25-O and 2A25-T651 are two conditions of the same aluminum grade, 2A25: O (annealed) versus T651 (T6, stress relieved by stretching). The chemistry is identical, so every difference below comes from the condition. 2A25-T651 is the stronger of the two: yield strength 400 MPa (58 ksi) against 105 MPa (15.2 ksi) for 2A25-O, about 3.8 times as much; tensile strength follows at 455 MPa (66 ksi) vs 215 MPa (31.2 ksi). In exchange, 2A25-O is the more ductile: elongation 18% versus 8% for 2A25-T651, and 2A25-T651 is harder (132 HB vs 50 HB). 2A25-O runs hotter in service (200°C vs 150°C continuous) and 2A25-O conducts heat better (190 W/m·K vs 155 W/m·K). On the shop floor, 2A25-T651 machines more easily (very good vs fair).
2A25-OChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
2A25-T651Choose it when strength drives the design, or when the part is machined in volume.
2A25-O vs 2A25-T651: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 72 GPa10.4 Msi · Shear Modulus 27 GPa3.9 Msi · Bulk Modulus 75 GPa10.9 Msi · Poisson's Ratio 0.33 · Fatigue Strength (Endurance Limit) 125 MPa18.1 ksi
Physical
Density and transition temperatures.
Same in both: Density 2.8 g/cm³0.1 lb/in³ · Melting Point (Solidus) 507°C945 °F · Liquidus Temperature 638°C1,180 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 880 J/kg·K0.21 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 22.5 µm/m·K12.5 µin/in·°F · Latent Heat of Fusion 390 J/g168 BTU/lb · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.69 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Formability (cold)
Same in both: Weldability 25 / 100 · Castability 20 / 100 · Brazeability / Solderability 15 / 100 · Polishability 55 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 200 MJ/kg85,985 BTU/lb · Embodied Carbon (primary production) 14 kg CO₂/kg · Embodied Water 1,100 L/kg132 gal/lb · Typical Recycled Content 15%
Strength versus weight
Yield strength against density for every aluminum grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
2A25-O vs 2A25-T651 — frequently asked
Is 2A25-T651 stronger than 2A25-O?
Yes. 2A25-T651 has a typical yield strength of 400 MPa (58 ksi) against 105 MPa (15.2 ksi) for 2A25-O — about 3.8 times as much. Tensile strength is 455 MPa (66 ksi) vs 215 MPa (31.2 ksi).
Which condition does FabDigit quote by default, O or T651?
T6 is the default 2A25 condition in the FabDigit quote flow (neither O nor T651). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 2A25-O or 2A25-T651?
2A25-T651. Its machinability rates very good (72/100) against fair (45/100) for 2A25-O.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 2A25-O and 2A25-T651 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.