Aluminum 2A21-T4 vs 2A21-T62
Aluminum · 2A21 temper comparison
2A21-T4 and 2A21-T62 are two conditions of the same aluminum grade, 2A21: T4 (solution heat treated and naturally aged) versus T62 (T6, heat treated by the user). The chemistry is identical, so every difference below comes from the condition. 2A21-T62 is the stronger of the two: yield strength 275 MPa (39.9 ksi) against 210 MPa (30.5 ksi) for 2A21-T4, about 31% more; tensile strength follows at 390 MPa (56.6 ksi) vs 350 MPa (50.8 ksi). In exchange, 2A21-T4 is the more ductile: elongation 16% versus 11% for 2A21-T62, and 2A21-T62 is harder (115 HB vs 100 HB). 2A21-T62 runs hotter in service (250°C vs 175°C continuous).
2A21-T4Choose it when the part is bent, formed or impact-loaded.
2A21-T62Choose it when strength drives the design, or when the part sees heat.
2A21-T4 vs 2A21-T62: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Hardness, Brinell
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 73 GPa10.6 Msi · Shear Modulus 27 GPa3.9 Msi · Bulk Modulus 75 GPa10.9 Msi · Poisson's Ratio 0.33
Physical
Density and transition temperatures.
Same in both: Density 2.84 g/cm³0.1 lb/in³ · Melting Point (Solidus) 543°C1,009 °F · Liquidus Temperature 643°C1,189 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 864 J/kg·K0.21 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 22.3 µm/m·K12.4 µin/in·°F · Latent Heat of Fusion 389 J/g167 BTU/lb · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.66 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Brazeability / Solderability 15 / 100 · Polishability 60 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 210 MJ/kg90,284 BTU/lb · Embodied Carbon (primary production) 12.5 kg CO₂/kg · Embodied Water 1,100 L/kg132 gal/lb · Typical Recycled Content 15%
Strength versus weight
Yield strength against density for every aluminum grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
2A21-T4 vs 2A21-T62 — frequently asked
Is 2A21-T62 stronger than 2A21-T4?
Yes. 2A21-T62 has a typical yield strength of 275 MPa (39.9 ksi) against 210 MPa (30.5 ksi) for 2A21-T4 — about 31% more. Tensile strength is 390 MPa (56.6 ksi) vs 350 MPa (50.8 ksi).
Which condition does FabDigit quote by default, T4 or T62?
T4 is the default 2A21 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
When should I choose 2A21-T4 over 2A21-T62?
Pick 2A21-T4 when the part is bent, formed or impact-loaded. Pick 2A21-T62 when strength drives the design, or when the part sees heat.