Aluminum 2036 T4-PB vs 2036-T6
Aluminum · 2036 temper comparison
2036 T4-PB and 2036-T6 are two conditions of the same aluminum grade, 2036: T4-PB (T4 + paint bake) versus T6 (solution heat treated and artificially aged). The chemistry is identical, so every difference below comes from the condition. 2036-T6 is the stronger of the two: yield strength 310 MPa (45 ksi) against 245 MPa (35.5 ksi) for 2036 T4-PB, about 27% more; tensile strength follows at 395 MPa (57.3 ksi) vs 365 MPa (52.9 ksi). In exchange, 2036 T4-PB is the more ductile: elongation 18% versus 12% for 2036-T6, and 2036-T6 is harder (110 HB vs 95 HB).
2036 T4-PBChoose it when the part is bent, formed or impact-loaded.
2036-T6Choose it when strength drives the design.
2036 T4-PB vs 2036-T6: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Hardness, Brinell
Same in both: Elastic (Young's) Modulus 70.3 GPa10.2 Msi · Shear Modulus 26.5 GPa3.8 Msi · Bulk Modulus 70 GPa10.2 Msi · Poisson's Ratio 0.33 · Fatigue Strength (Endurance Limit) 130 MPa18.9 ksi
Physical
Density and transition temperatures.
Same in both: Density 2.75 g/cm³0.1 lb/in³ · Melting Point (Solidus) 554°C1,029 °F · Liquidus Temperature 650°C1,202 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Same in both: Specific Heat Capacity 880 J/kg·K0.21 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 23.4 µm/m·K13 µin/in·°F · Latent Heat of Fusion 390 J/g168 BTU/lb · Max Service Temperature (continuous) 150°C302 °F · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.69 V · Corrosion Resistance 38 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Brazeability / Solderability 15 / 100 · Polishability 55 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 205 MJ/kg88,134 BTU/lb · Embodied Carbon (primary production) 12.5 kg CO₂/kg · Embodied Water 1,150 L/kg138 gal/lb · Typical Recycled Content 25%
Strength versus weight
Yield strength against density for every aluminum grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
2036 T4-PB vs 2036-T6 — frequently asked
Is 2036-T6 stronger than 2036 T4-PB?
Yes. 2036-T6 has a typical yield strength of 310 MPa (45 ksi) against 245 MPa (35.5 ksi) for 2036 T4-PB — about 27% more. Tensile strength is 395 MPa (57.3 ksi) vs 365 MPa (52.9 ksi).
Which condition does FabDigit quote by default, T4-PB or T6?
T4 is the default 2036 condition in the FabDigit quote flow (neither T4-PB nor T6). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which welds better, 2036 T4-PB or 2036-T6?
2036 T4-PB. Its weldability rates fair (35/100) against poor (30/100) for 2036-T6.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 2036 T4-PB and 2036-T6 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.