Aluminum 1100A-H14 vs 1100A-H18
Aluminum · 1100A temper comparison
1100A-H14 and 1100A-H18 are two conditions of the same aluminum grade, 1100A: H14 (strain hardened, half hard) versus H18 (strain hardened, full hard). The chemistry is identical, so every difference below comes from the condition. 1100A-H18 is the stronger of the two: yield strength 150 MPa (21.8 ksi) against 115 MPa (16.7 ksi) for 1100A-H14, about 30% more; tensile strength follows at 165 MPa (23.9 ksi) vs 125 MPa (18.1 ksi). In exchange, 1100A-H14 is the more ductile: elongation 9% versus 5% for 1100A-H18, and 1100A-H18 is harder (44 HB vs 32 HB). 1100A-H14 runs hotter in service (150°C vs 120°C continuous).
1100A-H14Choose it when the part is bent, formed or impact-loaded, or when the part sees heat.
1100A-H18Choose it when strength drives the design.
1100A-H14 vs 1100A-H18: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 69 GPa10 Msi · Shear Modulus 26 GPa3.8 Msi · Bulk Modulus 68 GPa9.9 Msi · Poisson's Ratio 0.33
Physical
Density and transition temperatures.
Same in both: Density 2.71 g/cm³0.1 lb/in³ · Melting Point (Solidus) 643°C1,189 °F · Liquidus Temperature 657°C1,215 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 904 J/kg·K0.22 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 23.6 µm/m·K13.1 µin/in·°F · Latent Heat of Fusion 397 J/g171 BTU/lb · Min Service Temperature -250°C-418 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 57 % IACS · Electrical Resistivity 3.02×10⁻⁸ Ω·m1.19 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.83 V · Corrosion Resistance 78 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Brazeability / Solderability 85 / 100 · Polishability 75 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 200 MJ/kg85,985 BTU/lb · Embodied Carbon (primary production) 11.5 kg CO₂/kg · Embodied Water 1,150 L/kg138 gal/lb · Typical Recycled Content 30%
Strength versus weight
Yield strength against density for every aluminum grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
1100A-H14 vs 1100A-H18 — frequently asked
Is 1100A-H18 stronger than 1100A-H14?
Yes. 1100A-H18 has a typical yield strength of 150 MPa (21.8 ksi) against 115 MPa (16.7 ksi) for 1100A-H14 — about 30% more. Tensile strength is 165 MPa (23.9 ksi) vs 125 MPa (18.1 ksi).
Which condition does FabDigit quote by default, H14 or H18?
H14 is the default 1100A condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 1100A-H14 or 1100A-H18?
1100A-H18, by a small margin. Both rate fair for machinability — 42/100 against 35/100 for 1100A-H14; for welding the order is 1100A-H14 first (excellent, 95/100) then 1100A-H18 (excellent, 90/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 1100A-H14 and 1100A-H18 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.