Tungsten Alloy W-25Re vs WVMA (Doped Non-Sag Tungsten)
Tungsten Alloy · grade comparison
Tungsten Alloy W-25Re and WVMA (Doped Non-Sag Tungsten) are both tungsten alloy grades. Both yield at about 1,850 MPa — strength does not separate them. W-25Re is the more ductile: elongation 4% versus 2.5% for WVMA (Doped Non-Sag Tungsten), and W-25Re is harder (620 HV vs 480 HV). W-25Re runs hotter in service (2,400°C vs 2,000°C continuous) and WVMA (Doped Non-Sag Tungsten) conducts heat better (168 W/m·K vs 45 W/m·K). On the shop floor, W-25Re welds better (fair vs poor).
W-25ReChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
W-25Re vs WVMA (Doped Non-Sag Tungsten): propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all tungsten alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all tungsten alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
W-25ReWVMA (Doped Non-Sag Tungsten)
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Poisson's Ratio
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Hardness, Vickers
Compressive Strength
Shear Strength
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell C
Same in both: Elastic (Young's) Modulus 400 GPa58 Msi · Shear Modulus 156 GPa22.6 Msi · Bulk Modulus 310 GPa45 Msi
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Max Service Temperature (continuous)
Min Service Temperature
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Same in both: Corrosion Resistance 60 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Brazeability / Solderability
Polishability
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every tungsten alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | W-25Re | WVMA (Doped Non-Sag Tungsten) |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$$$ High | $$$$ High |
| Min. machined wall | — | — |
| Best machined surface | — | — |
W-25Re vs WVMA (Doped Non-Sag Tungsten) — frequently asked
What is the difference between W-25Re and WVMA (Doped Non-Sag Tungsten)?
Tungsten Alloy W-25Re and WVMA (Doped Non-Sag Tungsten) are both tungsten alloy grades. Both yield at about 1,850 MPa — strength does not separate them. W-25Re is the more ductile: elongation 4% versus 2.5% for WVMA (Doped Non-Sag Tungsten), and W-25Re is harder (620 HV vs 480 HV).
Which is cheaper, W-25Re or WVMA (Doped Non-Sag Tungsten)?
Both sit in the same relative cost tier ($$$$, high); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which welds better, W-25Re or WVMA (Doped Non-Sag Tungsten)?
W-25Re. Its weldability rates fair (45/100) against poor (15/100) for WVMA (Doped Non-Sag Tungsten).
Ready to make it?
Upload a CAD file and FabDigit prices the part in W-25Re and WVMA (Doped Non-Sag Tungsten) side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.