Titanium Ti-6Al-4V ELI (Grade 23) AM Powder-SR vs Ti-6Al-4V ELI (Grade 23) AM Powder-STA
Titanium · Ti-6Al-4V ELI (Grade 23) AM Powder temper comparison
Ti-6Al-4V ELI (Grade 23) AM Powder-SR and Ti-6Al-4V ELI (Grade 23) AM Powder-STA are two conditions of the same titanium grade, Ti-6Al-4V ELI (Grade 23) AM Powder: SR (stress relieved) versus STA (solution treated and aged). The chemistry is identical, so every difference below comes from the condition. Ti-6Al-4V ELI (Grade 23) AM Powder-STA is the stronger of the two: yield strength 1,080 MPa (157 ksi) against 1,010 MPa (146 ksi) for Ti-6Al-4V ELI (Grade 23) AM Powder-SR, about 7% more; tensile strength follows at 1,170 MPa (170 ksi) vs 1,100 MPa (160 ksi). In exchange, Ti-6Al-4V ELI (Grade 23) AM Powder-SR is the more ductile: elongation 13% versus 10% for Ti-6Al-4V ELI (Grade 23) AM Powder-STA, and Ti-6Al-4V ELI (Grade 23) AM Powder-STA is harder (355 HB vs 330 HB). On the shop floor, Ti-6Al-4V ELI (Grade 23) AM Powder-SR welds better (very good vs good).
Ti-6Al-4V ELI (Grade 23) AM Powder-SRChoose it when the part is bent, formed or impact-loaded, or when it will be welded.
Ti-6Al-4V ELI (Grade 23) AM Powder-STAChoose it when strength drives the design.
Ti-6Al-4V ELI (Grade 23) AM Powder-SR vs Ti-6Al-4V ELI (Grade 23) AM Powder-STA: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all titanium grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all titanium grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Ti-6Al-4V ELI (Grade 23) AM Powder-SRTi-6Al-4V ELI (Grade 23) AM Powder-STA
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell C
Hardness, Vickers
Same in both: Shear Modulus 43 GPa6.2 Msi · Bulk Modulus 110 GPa16 Msi · Poisson's Ratio 0.34
Physical
Density and transition temperatures.
Same in both: Density 4.43 g/cm³0.16 lb/in³ · Melting Point (Solidus) 1,604°C2,919 °F · Liquidus Temperature 1,660°C3,020 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Same in both: Specific Heat Capacity 560 J/kg·K0.13 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 8.7 µm/m·K4.8 µin/in·°F · Latent Heat of Fusion 365 J/g157 BTU/lb · Max Service Temperature (continuous) 350°C662 °F · Min Service Temperature -253°C-423 °F
Electrical
Conductivity and insulation.
Electrical Resistivity
Same in both: Electrical Conductivity 1 % IACS
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.1 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Brazeability / Solderability 40 / 100 · Polishability 75 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 780 MJ/kg335,340 BTU/lb · Embodied Carbon (primary production) 48 kg CO₂/kg · Embodied Water 400 L/kg47.9 gal/lb · Typical Recycled Content 20%
Strength versus weight
Yield strength against density for every titanium grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Ti-6Al-4V ELI (Grade 23) AM Powder-SR vs Ti-6Al-4V ELI (Grade 23) AM Powder-STA — frequently asked
Is Ti-6Al-4V ELI (Grade 23) AM Powder-STA stronger than Ti-6Al-4V ELI (Grade 23) AM Powder-SR?
Yes. Ti-6Al-4V ELI (Grade 23) AM Powder-STA has a typical yield strength of 1,080 MPa (157 ksi) against 1,010 MPa (146 ksi) for Ti-6Al-4V ELI (Grade 23) AM Powder-SR — about 7% more. Tensile strength is 1,170 MPa (170 ksi) vs 1,100 MPa (160 ksi).
Which condition does FabDigit quote by default, SR or STA?
SR is the default Ti-6Al-4V ELI (Grade 23) AM Powder condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which welds better, Ti-6Al-4V ELI (Grade 23) AM Powder-SR or Ti-6Al-4V ELI (Grade 23) AM Powder-STA?
Ti-6Al-4V ELI (Grade 23) AM Powder-SR. Its weldability rates very good (75/100) against good (60/100) for Ti-6Al-4V ELI (Grade 23) AM Powder-STA.
Ready to make it?
Upload a CAD file and FabDigit prices the part in Ti-6Al-4V ELI (Grade 23) AM Powder-SR and Ti-6Al-4V ELI (Grade 23) AM Powder-STA side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.