Steel X15CrMo5-1-A vs X15CrMo5-1 QT-BOLT
Steel · X15CrMo5-1 temper comparison
X15CrMo5-1-A and X15CrMo5-1 QT-BOLT are two conditions of the same steel grade, X15CrMo5-1: A (solution annealed) versus QT-BOLT (+QT bolting condition). The chemistry is identical, so every difference below comes from the condition. X15CrMo5-1 QT-BOLT is the stronger of the two: yield strength 580 MPa (84.1 ksi) against 330 MPa (47.9 ksi) for X15CrMo5-1-A, about 76% more; tensile strength follows at 750 MPa (109 ksi) vs 550 MPa (79.8 ksi). In exchange, X15CrMo5-1-A is the more ductile: elongation 26% versus 18% for X15CrMo5-1 QT-BOLT, and X15CrMo5-1 QT-BOLT is harder (230 HB vs 170 HB). On the shop floor, X15CrMo5-1-A machines more easily (good vs fair).
X15CrMo5-1-AChoose it when the part is bent, formed or impact-loaded, or when the part is machined in volume.
X15CrMo5-1 QT-BOLTChoose it when strength drives the design.
X15CrMo5-1-A vs X15CrMo5-1 QT-BOLT: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
X15CrMo5-1-AX15CrMo5-1 QT-BOLT
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell C
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 213 GPa30.9 Msi · Shear Modulus 82 GPa11.9 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29
Physical
Density and transition temperatures.
Same in both: Density 7.78 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,425°C2,597 °F · Liquidus Temperature 1,510°C2,750 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Same in both: Specific Heat Capacity 470 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 11.5 µm/m·K6.4 µin/in·°F · Latent Heat of Fusion 270 J/g116 BTU/lb · Max Service Temperature (continuous) 550°C1,022 °F · Min Service Temperature -30°C-22 °F
Electrical
Conductivity and insulation.
Electrical Resistivity
Same in both: Electrical Conductivity 3.1 % IACS
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.6 V · Corrosion Resistance 25 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Brazeability / Solderability 50 / 100 · Polishability 55 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 34 MJ/kg14,617 BTU/lb · Embodied Carbon (primary production) 2.5 kg CO₂/kg · Embodied Water 60 L/kg7.2 gal/lb · Typical Recycled Content 25%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
X15CrMo5-1-A vs X15CrMo5-1 QT-BOLT — frequently asked
Is X15CrMo5-1 QT-BOLT stronger than X15CrMo5-1-A?
Yes. X15CrMo5-1 QT-BOLT has a typical yield strength of 580 MPa (84.1 ksi) against 330 MPa (47.9 ksi) for X15CrMo5-1-A — about 76% more. Tensile strength is 750 MPa (109 ksi) vs 550 MPa (79.8 ksi).
Which condition does FabDigit quote by default, A or QT-BOLT?
NT is the default X15CrMo5-1 condition in the FabDigit quote flow (neither A nor QT-BOLT). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, X15CrMo5-1-A or X15CrMo5-1 QT-BOLT?
X15CrMo5-1-A. Its machinability rates good (55/100) against fair (40/100) for X15CrMo5-1 QT-BOLT; for welding the order is X15CrMo5-1-A first (fair, 45/100) then X15CrMo5-1 QT-BOLT (fair, 40/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in X15CrMo5-1-A and X15CrMo5-1 QT-BOLT side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.