Steel X12Ni5-A vs X12Ni5 FORGED-QT
Steel · X12Ni5 temper comparison
X12Ni5-A and X12Ni5 FORGED-QT are two conditions of the same steel grade, X12Ni5: A (solution annealed) versus FORGED-QT. The chemistry is identical, so every difference below comes from the condition. X12Ni5 FORGED-QT is the stronger of the two: yield strength 420 MPa (60.9 ksi) against 340 MPa (49.3 ksi) for X12Ni5-A, about 24% more; tensile strength follows at 600 MPa (87 ksi) vs 520 MPa (75.4 ksi). In exchange, X12Ni5-A is the more ductile: elongation 28% versus 22% for X12Ni5 FORGED-QT, and X12Ni5 FORGED-QT is harder (180 HB vs 155 HB).
X12Ni5-AChoose it when the part is bent, formed or impact-loaded.
X12Ni5 FORGED-QTChoose it when strength drives the design.
X12Ni5-A vs X12Ni5 FORGED-QT: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 205 GPa29.7 Msi · Shear Modulus 79 GPa11.5 Msi · Bulk Modulus 165 GPa23.9 Msi · Poisson's Ratio 0.29
Physical
Density and transition temperatures.
Same in both: Density 7.85 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,440°C2,624 °F · Liquidus Temperature 1,500°C2,732 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Same in both: Specific Heat Capacity 470 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 11.2 µm/m·K6.2 µin/in·°F · Latent Heat of Fusion 270 J/g116 BTU/lb · Max Service Temperature (continuous) 350°C662 °F · Min Service Temperature -120°C-184 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.6 V · Corrosion Resistance 16 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Brazeability / Solderability 55 / 100 · Polishability 60 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 38 MJ/kg16,337 BTU/lb · Embodied Carbon (primary production) 3 kg CO₂/kg · Embodied Water 65 L/kg7.8 gal/lb · Typical Recycled Content 25%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
X12Ni5-A vs X12Ni5 FORGED-QT — frequently asked
Is X12Ni5 FORGED-QT stronger than X12Ni5-A?
Yes. X12Ni5 FORGED-QT has a typical yield strength of 420 MPa (60.9 ksi) against 340 MPa (49.3 ksi) for X12Ni5-A — about 24% more. Tensile strength is 600 MPa (87 ksi) vs 520 MPa (75.4 ksi).
Which condition does FabDigit quote by default, A or FORGED-QT?
QT is the default X12Ni5 condition in the FabDigit quote flow (neither A nor FORGED-QT). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, X12Ni5-A or X12Ni5 FORGED-QT?
X12Ni5-A. Its machinability rates good (60/100) against fair (51/100) for X12Ni5 FORGED-QT; for welding the order is X12Ni5-A first (very good, 72/100) then X12Ni5 FORGED-QT (good, 66/100).