Steel WCB Q&T vs WCB
Steel · WCB temper comparison
WCB Q&T and WCB are two conditions of the same steel grade, WCB: Q&T (quenched and tempered) versus WCB (ASTM A216 Grade WCB, normalized (or N+T), standard valve-body grade). The chemistry is identical, so every difference below comes from the condition. WCB Q&T is the stronger of the two: yield strength 380 MPa (55.1 ksi) against 290 MPa (42.1 ksi) for WCB, about 31% more; tensile strength follows at 585 MPa (84.8 ksi) vs 520 MPa (75.4 ksi). In exchange, WCB is the more ductile: elongation 28% versus 24% for WCB Q&T, and WCB Q&T is harder (180 HB vs 150 HB).
WCB Q&TChoose it when strength drives the design.
WCBChoose it when the part is bent, formed or impact-loaded.
WCB Q&T vs WCB: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 202 GPa29.3 Msi · Shear Modulus 78 GPa11.3 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29
Physical
Density and transition temperatures.
Same in both: Density 7.85 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,425°C2,597 °F · Liquidus Temperature 1,510°C2,750 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Same in both: Specific Heat Capacity 486 J/kg·K0.12 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 11.9 µm/m·K6.6 µin/in·°F · Latent Heat of Fusion 272 J/g117 BTU/lb · Max Service Temperature (continuous) 425°C797 °F · Min Service Temperature -29°C-20 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.61 V · Corrosion Resistance 12 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Castability 80 / 100 · Brazeability / Solderability 55 / 100 · Polishability 50 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 24 MJ/kg10,318 BTU/lb · Embodied Carbon (primary production) 1.9 kg CO₂/kg · Embodied Water 60 L/kg7.2 gal/lb · Typical Recycled Content 85%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
WCB Q&T vs WCB — frequently asked
Is WCB Q&T stronger than WCB?
Yes. WCB Q&T has a typical yield strength of 380 MPa (55.1 ksi) against 290 MPa (42.1 ksi) for WCB — about 31% more. Tensile strength is 585 MPa (84.8 ksi) vs 520 MPa (75.4 ksi).
Which condition does FabDigit quote by default, Q&T or WCB?
WCB is the default WCB condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, WCB Q&T or WCB?
WCB. Its machinability rates good (58/100) against fair (52/100) for WCB Q&T; for welding the order is WCB first (very good, 80/100) then WCB Q&T (very good, 75/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in WCB Q&T and WCB side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.